Abstract:Highly ordered TiO2 nanotube array electrodes were successfully fabricated by a two-step anodization method on Ti sheet substrates in an electrolyte composed of ammonium fluoride, deionized water, and glycol. The tube wall was smooth, and the average internal and external diameters, wall thickness, and tube length achieved were 80 nm, 90 nm, 10 nm, and 9 μm, respectively. X-ray diffraction and field emission scanning electron microscopy results revealed that the TiO2 nanotube arrays presented an amorphous structure. When calcined at 300 °C, the arrays crystallized into the anatase phase, and the crystallization degree of the oxide layer increased as the temperature rose. Calcinating at 400 °C did not obviously disrupt the porous structure of the highly ordered arrays. However, higher temperature enlarged the diameter of the nanotube array and roughened the tube wall. When the temperature reached 600 °C, the nanotube mouth broke because of the excessive stress, causing the oxide layer’s thinness and nanotube mouth clogging. The photoelectric test showed that the electrode presented obvious photoresponse under 300–400 nm UV excitation (maximized at 360 nm). The degree of crystallization and the micro-structure of the oxide layer can significantly affect the photoelectric properties of the electrode. After calcination at 400 °C, the TiO2 nanotube arrays, with highly ordered tubular structure directly connected to the Ti substrate, can ensure the rapid transportation of photo-induced electrons to the Ti substrate, while the high crystallinity of the arrays can help reduce the defect density of the nanotube and extend the lifetime of the photo-induced carriers. The electrode showed the best photoelectric property, and the photocurrent intensity was maximized (29.6 μA). However, the calcination process with over-temperature resulted in substantial loss of the TiO2 oxide layer, mouth clogging, and a severe decline in the photoelectric properties.

Characteristics of two-dimensional millimetric microarrays of TiO2 nanowires and their photocatalytic properties

Surface roughening and top opening of single crystalline TiO2 nanowires for enhanced photocatalytic activity

Activation of Carbon Cloth and Concurrent Precipitation of Titania Nanowires for Enhanced Adsorption and Photocatalysis Performance

Photocatalytic Active Titania Nanowire Arrays on Ti Substrates

A novel approach to titania nanowire arrays as photoanodes of back-illuminated dye-sensitized solar cells

Synthesis, Characterization and Photocatalytic Activity of Hierarchical Spherical TiO2 Nanostructures

Univariate Lattice Parameter Modulation of Single-Crystal-like Anatase TiO2 Hierarchical Nanowire Arrays to Improve Photoactivity

Porous TiO2 Nanowires Derived from Nanotubes: Synthesis, Characterzation and Their Enhanced Photocatalytic Properties

One-dimensional TiO2 nanomaterials: preparation and catalytic applications.

In Situ Synthesis and Characterization of TiO 2 Nanoarray Films

Preparation And Characterization Of Tio2 Nanorod Arrays Via Hydrothermal Approach

Fabrication of TiO2 Nanowire Arrays Using Laser Interference Lithography Aided Hydrothermal Method

From nanorods to atomically thin wires of anatase TiO(2): nonhydrolytic synthesis and characterization.

Titanium Dioxide Nano-Heterostructure with Nanoparticles Decorating Nanowires for High-Performance Photocatalysis

Fabrication,modification of TiO2 nanotube arrays and their research progress in application

Tube-In-Tube Tio2 Nanotubes with Porous Walls: Fabrication, Formation Mechanism, and Photocatalytic Properties

Preparation and Characterization of Anatase TiO2 Nanowires Using Hydrothermal Synthesis Method

Study on Fabrication and UV Photoelectric Property of TiO2 Nanotube Array Electrodes.

A Facile Route to Synthesis of Double-Sided TiO2 Nanotube Arrays for Photocatalytic Activity

Synthesis of anatase titania-carbon nanotubes nanocomposites with enhanced photocatalytic activity through a nanocoating-hydrothermal process

Enhanced photoelectrochemical and photocatalytic performance of single-crystalline anatase TiO2 (1 0 1) nanobelts arrays originating from nanotubes arrays