Studies on Polymer-coated Gold Nanoparticles with Temperature Sensitive and Intelligent Fluorescent Properties
Chun-hua Luo,Qiu-jing Dong,Rong-rong Han,Hong-tao Wang,Rong-can Yin,Hong Zhang
DOI: https://doi.org/10.11777/j.issn1000-3304.2015.14319
2015-01-01
Acta Polymerica Sinica
Abstract:Polymer-coated gold nanoparticles (PNIPAM-AuNPs) with temperature sensitive and intelligent fluorescent properties were prepared by ligand exchange between dimethylaminochalcone-terminated poly(N-isopropylacrylamide) (PNIPAM-DMAC) and 4-dimethylaminopyridine-stabilized gold nanoparticles (DMAP-AuNPs) precursor, and the morphology and structure of the as-prepared AuNPs were analyzed by UV-Vis, TEM, H-NMR, FTIR and TGA. The as-synthesized PNIPAM-AuNPs can be well dispersed not only in water but also in ethanol, acetone, chloroform and tetrahydrofuran, and the corresponding characteristic peak of the surface plasmon resonance (SPR) absorption of the PNIPAM-AuNPs is observed at 537 nm,527. 6 nm, 527. 4 nm, 532. 2 nm and 530. 4 nm respectively. The surface grafting density of PNIPAM-DMAC is 1-2 polymer chains/nm(2). The results of thermosensitive properties show that PNIPAM-AuNPs have a lower critical solution temperature (LCST) 2. 5 K lower than that of PNIPAM-DMAC, and the SPR absorption peak of PNIPAM-AuNPs blueshifts to 525 nm from 537 nm after the phase transition. With the increase of the solvent polarity, the fluorescence characteristic wavelength of PNIPAM-AuNPs redshifts, and the fluorescence intensity first increases then decreases, which indicates solvent polarity sensitive fluorescence properties of PNIPAM-AuNPs. There are no fluorescent emitting properties of PNIPAM-AuNPs aqueous solution at 25 CC, while at 45 CC the fluorescence intensity of PNIPAM-AuNPs enhances obviously,which endows PNIPAM-AuNPs with temperature "on/off" fluorescent properties.