Abstract:The purpose of this paper is to understand the softening extent and stress-strain behavior of the normal-strength 6061-T6, 6013-T6, and high-strength 7075-T6 aluminium alloy butt joints using the novel friction stir welding (FSW) technique. A total of 107 monotonic tensile coupons and 33 Vickers hardness coupons were prepared from 8- or 12-mm thick welded plates using various tool rotation speed, welding transverse speed and tool configurations. The surface morphology, stress-strain curves and hardness distribution laws after welding were evaluated. The W-shaped hardness profiles were clearly observed, with the fracture location positively correlated at the lowest point of Vickers hardness near the edge of the weld toe. The strength reduction and softening extent of extruded aluminium alloys in T6 temper induced by FSW were superior to those of aluminium alloys using fusing welding process outlined in the Chinese and European standards, indicating the effectiveness and applicability of the FSW technique in the formation of components and connections for aluminium alloy structures. Additionally, the current widely used constitutive models generally yielded under-estimations on the strength under large strains. The developed three-stage Ramberg-Osgood model, using seven key input parameters, significantly improved the accuracy and consistent predictions in the full-range stress-strain curve of FSW aluminium alloys. Furthermore, the suggested model could still achieve a great balance between accuracy and practicality when using just three common available parameters with the employment of predictive expressions on other four parameters.

Microstructure and microhardness of aluminium alloy friction stir welds with heat treatment

Parameters Controlling Microstructure and Hardness During Friction-Stir Welding of Precipitation-Hardenable Aluminum Alloy 6063

Friction-Stir Welding of a Wrought Al-Si-Mg Alloy in As-Fabricated and Heat-Treatment States

Effects of Post-Weld Heat Treatment on Microstructure and Mechanical Properties of Friction Stir Welded Joints of 2219-O Aluminium Alloy

Characteristics of Microstructure and Microhardness of Friction Stir Welded Joints for AZ31 Magnesium Alloy

Effect of Heat Treatment on Tensile Properties of Friction Stir Welded Joints of 2219-T6 Aluminium Alloy

Effect of Heat Treatment on the Microstructure and Properties of a Ti<sub>3</sub>Al Linear Friction Welding Joint

Effect Of Heat Treatment On The Microstructure And Properties Of A Ti3al Linear Friction Welding Joint

Effect of Post-Processing Heat Treatment on Microstructure and Microhardness of Water-Submerged Friction Stir Processed 2219-T6 Aluminum Alloy

Effects of Solution Heat Treatment on Friction Stir Welding Joints of 7B04-O Aluminum Alloy

Residual Stress, Microstructure and Mechanical Properties in Thick 6005A-T6 Aluminium Alloy Friction Stir Welds

Relationship Between Microstructures and Microhardness in High-Speed Friction Stir Welding of AA6005A-T6 Aluminum Hollow Extrusions

Microstructural evolution of 6063 aluminum during friction-stir welding

The Effect of Postprocessing on Tensile Property and Microstructure Evolution of Friction Stir Welding Aluminum Alloy Joint

Experimental Study on Mechanical Behaviour of Friction Stir Welded Aluminium Alloy Butt Joints

Influence of Welding Combined Plastic Forming on Microstructure Stability and Mechanical Properties of Friction Stir-Welded Al-Cu Alloy

Effect of Heat Treatment on the Microstructure and Vickers Hardness of Aluminum Alloy Gradient Plate Prepared Through Friction Stir Processing

Influence of Material Properties on Microstructure and Mechanical Properties of Aluminum Alloy FSW Joints

Microstructure and Mechanical Behavior of Friction Stir-Welded Sc-Modified Al-Zn-Mg Alloys Made Using Different Base Metal Tempers

Microstructural Characteristics and Mechanical Properties of Friction Stir Spot Welded 2A12-T4 Aluminum Alloy

Microstructures and Mechanical Properties of Al-Li Alloy Friction Stir Weld