Manipulated Crystallization and Passivated Defects for Efficient Perovskite Solar Cells via Addition of Ammonium Iodide
Wenjing Qi,Jiale Li,Yameng Li,Khumal Sohail,Hao Ling,Peng Wang,Sumin Jiao,Fan Liu,Xin Zhou,Huanhuan Wang,Dekun Zhang,Yi Ding,Xinliang Chen,Guofu Hou,Jingshan Luo,Ying Zhao,Yuelong Li,Xiaodan Zhang
DOI: https://doi.org/10.1021/acsami.1c05903
2021-07-13
Abstract:Organic–inorganic metal halide perovskite materials have been widely studied as the light absorber for efficient photovoltaics. However, perovskite layers with defective nature are typically prepared with an uncontrollable crystallization process, intrinsically limiting further advance in device performance, and thus require delicate manipulation of crystallization processes and defect density. Here, we demonstrate an ammonium-assisted crystallization of perovskite absorbers during a two-step deposition to fabricate efficient solar cells. Addition of ammonium iodide (NH<sub>4</sub>I) is devised to manipulate the nucleation and crystal growth of perovskite, wherein the formation and transition of intermediate <i>x</i>[NH<sub>4</sub><sup>+</sup>]•[PbI<sub>3</sub>]<sup><i>x</i>−</sup> enables high-quality perovskite layers with an enlarged grain and reduced defect density. As a result, the perovskite solar cells (PSCs) achieve an average efficiency of 21.36% with a champion efficiency of 22.15% and improved environmental stability over 30 days in ambient conditions with varied relative humidity. These results with addition of NH<sub>4</sub>I provide an available and ingenious way to construct high-quality perovskite layers for efficient solar cells and will advance the commercial application of perovskite-based photovoltaics.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acsami.1c05903?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acsami.1c05903</a>.Experiment method; (Figure S1) SEM images, (Figure S3) absorption, (Figure S4) PL and TRPL of the perovskite layer with different concentrations of NH<sub>4</sub>I; (Figure S2) XRD and SEM images of PbI<sub>2</sub> with or without NH<sub>4</sub>I; (Figure S5 and Table S1) photovoltaic parameter distribution of PSCs with different concentrations of NH<sub>4</sub>I; (Figure S6) PCE distribution and MPP tracking of PSCs with and without NH<sub>4</sub>I addition; (Figure S7 and Table S2) photovoltaic parameter distribution of PSCs with NH<sub>4</sub>I added on different functional layers; (Figure S8) fitted dark <i>J–V</i>; and (Table S3) fitted parameters of EIS (<a class="ext-link" href="/doi/suppl/10.1021/acsami.1c05903/suppl_file/am1c05903_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.
materials science, multidisciplinary,nanoscience & nanotechnology