Preliminary Study of Surface-Enhanced Raman Scattering from Bare Zinc Electrode
Xiaoying Shen,G. K. Liu,Ruiting Gu,ZQ Tian
DOI: https://doi.org/10.1071/sa0402116
2004-01-01
Abstract:Using confocal Raman microscopy, potential dependent surface enhanced Raman spectra (SERS) of pyridine adsorbed on a bare zinc (Zn) bulk electrode were observed for the first time and the adsorption behaviour of pyridine on zinc was discussed. Electrochemical oxidationreduction method was employed to roughen Zn electrode for obtaining SERS from it. Surface-enhanced Raman spectroscopy (SERS) has been developed as a useful in situ tool for providing bonding information between adsorbates and substrates since it was originally found in 1970s[1]. During last thirty years, numerous researchers in this field have been making efforts to extend its application due to its high sensitivity and selectivity[2,3]. Zinc has been used extensively as electrodes for primary and secondary batteries (Zn-Ni, Znair, Zn-Ag and Zn-MnO2 batteries etc.) because of its high specific energy density, high hydrogen over-potential, low cost and ease of handling[4]. Zinc is more active than iron, and it can be easily oxidized in the air or some corrosive environment, so it is often used as a sacrificial protective coating to prevent corrosion of steel (galvanized steel) exposed to water. A large number of conventional electrochemical and spectroscopic techniques have been employed to study the corrosion behavior of zinc in neutral solutions or humid atmosphere and its passivation in alkaline electrolytes [5,6]. For zinc, enhanced Raman spectra of CN adsorbed on thin Zn layers deposited from cyanide plating baths onto silver substrate had been obtained by Fleischmann et al [7]. Recently, Cai et al electrodeposited silver on Zn electrodes to enhance the rather weak Raman signal of passive film for studying the behavior of zinc electrodes in alkaline solutions. It was found that this procedure was effective for experiments performed in the more concentrated KOH solutions, but the attempts to utilize it for more dilute KOH solutions, i.e. 0.1M, were not very successful because of the lack of adherence of the Ag particles to the substrate [8]. This is not appropriate for studying surface adsorption because one can not assure that adsorbate was only adsorbed at zinc surface and exclude the great enhancement of Ag. It is apparent that the most convincing and challenging method is to obtain SERS from the bare metal surface directly. Here, we present a study of surface Raman spectroscopy from bare Zn electrode by proper roughening process. It has been reported that chemical etching or electrochemical oxidation-reduction cycle (ORC) or the combination of them can be used effectively for the roughening of transition metals such as Fe, Co, Ni [3]etc.. Chemical etching has been considered as the simplest method for creating SERS-active substrate, therefore, as the first try, we used H2SO4 solution to roughen Zn electrodes. Unfortunately, no discernible surface Raman signal of pyridine can be observed. As an alternative way to roughen the metal surface, one can use electrochemical ORC method. Two methods, the linear sweep method and the double step method, have been found that can roughen effectively the Zn electrode while presenting reasonable SERS activity. In both methods, a neutral NaClO 4 solution was used as the electrolyte. The linear sweep is to sweep the potential of the Zn electrode between -1.6 V and -0.7 V at a rate of 50 mVs for several cycles to allow the oxidation and reduction of the electrode surface. Finally, the electrode was held at -1.6 V for several minutes to reduce the zinc oxide on the surface completely. A detailed analysis of the cyclic voltammetric