Abstract:The fracture behavior at crack tip within CMn steel is analyzed based on the experiments of 3 PB precracked specimens and FEM calculation and simulation. The results show that before a critical load is reached, the crack tip is blunted only and in its vicinity the three criteria of cleavage fracture are satisfied in different regions separated from each other. The nucleated cracks cannot propagate and the cleavage fracture cannot be triggered. With the applied load increasing higher than this critical load, a short crack is initiated and extended at the precrack tip and then is blunted again. While the plastic strain remains in front of the tip, the stress triaxiality is released and then rebuilt. Under the second critical load, the regions, where the three criteria are satisfied, are overlapped each other and cleavage crack is nucleated and propagates. The minimum distance for cleavage fracture is that on where the overlapping of abovementioned regions begins. Combined with the three criteria previously mentional, the fracture behavior at crack tip and the corresponding changes of driving forces (ep,σm/σe and σyy) provide a complete physical model of cleavage fracture of steels on a local scale.

Study of Fracture Behavior at Crack Tip Within C-Mn Steel