Influence of TiO_2 Nanocrystals with Difference Morphologies on Photoluminescence Properties

Zhiyu Wang

2010-01-01

Nanoscience and Nanotechnology

Abstract:Four morphologies of anatase TiO_2 nanocrystals including quasi—sphere,rod,mixture of quasi-sphere and rod, and rhombus with well—uniform diameter less than 50 nm,were successfully prepared by solvothermal method.UV—vis absorption and PL.(photoluminescence) were employed to characterize the absorbance and photoluminescence intensity of as-prepared TiO_2 nanocrystals.The PL spectra excited at 330 nm exhibits four peaks at 345 nm.363 nm,380 nm and 402 nm.We firstly discovered and proved the direct transitions X_(1b)→X_(2b)(345 nm) and X_(1b)→X_(1a)(363 nm).This phenomenon results from the changes of TiO_2 nanocrystals {001} family planes' surface situations which caused by oleic acid.The UV absorption peaks of TiO_2 nanocrystals locale at 229 nm.which in not relevant to their morphologies.The calculated value of the as-prepared TiO_2 nanocrystals were close to the theoretical value about 3.2 eV.