Abstract:The microstructure ,crack shape, appearance of the fracture and the hardness of the piston rod were studied with the help of optical microscope and scanning electron microscope (SEM). The reasons resulting in rupture of the piston rod were analyzed. The preliminary research showed that the material used of the piston rod is unqualified ,casting aliquation and much S element result in cracking on the edge of the casting aliquation. Hardness is more than the ruled value due to poor heat treatment conditions, thereofore ,under the action of axial stress, the cracks grow on the direction which is normal to axes until the rupture of the rod takes place.

Rupture Research of 40crmnmo Piston-Rod