THE STUDY ON ENHANCING THE CRITICAL CURRENT DENSITY J_c OF THE MTG YBCO AND GdBCO SUPERCONDUCTORS BY THERMAL NEUTRON IRRADIATION

Jian Li

1993-01-01

Abstract:It is proved that the neutron irradiation on the high T_c superconductors is one of the most ef-fective methods to increase their critical current. In the paper, the effect of the thermal neutronirradiation on critical current density J_c of Melt-Textured Growth (MTG) YBa_2Cu_3O_(7-y) andGdBa_2Cu_3O_(7-y) superconductors are studied systematically within a horizontal beam hole of theHeavy Water Research Reactor(HWRR). Neutron irradiation experiments include eight samples of YBCO with thermal neutron fluences from 3.7×10~(11) to 1.4×10~(17)cm~(-2) and six samples ofGdBCO with thermal neutron fluences from 5.2×10~(13) to 4.7×10~(17)cm~(-2). For all MTG supercon-ductive samples, the critical current density J_c, which are determined by the hysteresis loops mea-sured by a moving sample magnetometer, are compared before and after irradiation. The results ofYBCO show that the J_c values of irradiated samples with thermal neutron fluence of 10~(17)cm~(-2) aretwice as high as that of unirradiated samples, and the results of GdBCO also show that the J_c val-ue are enhanced significantly. It is found that the increments of the J_c of irradiated samples are in-creasing with the augmentation of the thermal neutron fluence and the increment of the J_c in high-er magnetic field is larger than that in lower magnetic field. This phenomenon seems to be ex-plained as follows. With the augmentation of the thermal neutron fluence, the increase of thecrystal defects as flux pinning centers is increasing, namely the density of flux pinning centers isincreasing and the distance between pinning centers is shortened, so as to be advantageous to thepinning function at higher magnetic field.