Synthesis and Properties of a Zwitterionic Copolymer Containing Phosphate Group
Shao-hua GOU,Yu-mei FEI,Qin ZHANG,Hao LUO,Wei LUO,Ting-ting WANG,Wen-chao XIE
DOI: https://doi.org/10.13550/j.jxhg.2018.01.021
2018-01-01
Abstract:A water-soluble zwitterionic copolymer (ANND) was synthesized with acrylamide (AM), acrylic acid (AA), N-(3-methacrylamidopropyl)-N, N-dimethylheptadecan-1-aminium bromide (NADA) and 1-dimethylaminoallyl phosphoric acid (DMAAPA) And then it was evaluated as an oil-displacing agent.The copolymer was characterized by FTIR,and the content of NADA and DMAAPA, the mass ratio between NADA and DMAAPA,the initiator dosage and the temperature were varied step by step to investigate their influence on the intrinsic viscosity of copolymer.Moreover,the properties of copolymer (salt tolerance temperature resistance,rheology and so on) were discussed The results showed that the as-prepared copolymer exhibited a good solubility in water.At 25 ℃ and 500 s-1the apparent viscosity of 2000 mg/L copolymer solution was 28.46 mPa·s,higher than that of 2000 mg/L HPAM (molecular weight of 10 million) solution (23.10 mPa·s). At 100 ℃ and 170 s-1,the apparent viscosity of copolymer solution was 40.48 mPa·s,while that of HPAM solution was only 31.31 mPa·s Furthermore,when the above-mentioned solutions were kept in water bath at 80 ℃ for 10 days the viscosity retention rate of copolymer solution was 38% which was higher than that of HPAM solution (17%) And the apparent viscosity of 2000 mg/L copolymer in 30000 mg/L NaCl,2 000 mg/L CaCl2and 2 000 mg/L MgCl2solutions was 28.9,32.1,30.7 mPa·s,respectively At the same condition,that of HPAM was 9.8,17.7 and 16.3 mPa·s.The stimulating displacement experiment indicated that the recovery ratio of 2000 mg/L copolymer solution was 55.67%,greater than that of 2000 mg/L HPAM solution (48.94%) and water (41.37%).