Abstract:Effect of reduction ratio in secondary cold-rolling on microstructure and texture of V and Ti contained grain-oriented silicon steel produced by TSCR process imitated in laboratory were researched.The results show that there will be intensive shearing stripe in the 60% cold-rolled microstructure,which is the best favorable in coldrolled plates for obtaining accurate Gaussian texture.With the magnifying of cold-rolling reduction ratio,the main texture type will transform fromαtexture toα+γtexture in the first cold-rolled plates.On the other hand,γtexture become the main texture in the secondary cold-rolling plates.And the higher cold-rolled reduction ratio,the moreγtexture.For example,fraction of{111}〈112〉will be 4.135 when cold-rolling reduction ratio is 60%,but it will not be enlarged too much above 60%.At last,with the experiment condition,the best first rolling ratio is 72% and the best secondary rolling ratio is 60%.With these experimental conditions,the secondary recrystallization of samples were impeccable and the best magnetic property will be obtained,whose P17 is 1.049 W/kg and B8 is 1.950 T.

Effect of Reduction Ratio in Secondary Cold-rolling on Microstructure and Texture of V and Ti-contained Grain-oriented Silicon Steel