Modification of High-Density Polyethylene/Scrap Rubber Powder Composites

李岩,张勇,张隐西

DOI: https://doi.org/10.19491/j.issn.1001-9278.2002.12.018

2002-01-01

Abstract:The effects of the loadings of EPDM,silicone oil and DCP on the mechanical properties of high-density polyethylene/scrap rubber powder(HDPE/SRP)were investigated.Results show that the optimum loadings of EPDM,silicone oil and DCP were 10～15phr,4phr and 0.2phr respectively,under which the composites possessed preferable mechanical properties.The impact strength and elongation at break of the modified composites(modified with10phr EPDM,4phr silicone oil and 0.2phr DCP)were much higher than those of the unmodified composites(HDPE/SRP).At the same time,the extent of increase of the impact strength and elongation at break was higher for the modified composites with smaller content of SRP.Scanning electric morphology(SEM)observation shows that EPDM existed in resin with two types of structure:separate dispersion and encapsulation around SRP,which might result in good toughness of the modified composites.