Phenotypic variation of wood properties in a F1 pedigree of Salix suchowensis

GUO Zeng-chao,GUO Wei,HOU Jing,YIN Tong-ming,CHEN Ying-nan

DOI: https://doi.org/10.14067/j.cnki.1673-923x.2014.02.016

2014-01-01

Abstract:By taking a F1 pedigree of Salix suchowensis as the tested materials, the basic density and chemical compositions(content of cellulose, hemicellulose and lignin) of 132 progeny in a F1 pedigree of Salix suchowensis were measured, and the measured data were statistically analyzed. The results show that the average content of cellulose, hemicellulose and lignin were 53.19%, 19.80% and 14.20% respectively and their variation ranges were 47.91% ~ 57.00%, 12.28% ~ 16.43%, and 16.52% ~ 23.76% respectively; the basic wood density was 0.392 6 g/cm3, ranging from 0.241 6 g/cm3 to 0.504 4 g/cm3, the wood properties stated clearly that the aforementioned traits varied with a larger variation range among the progeny of the F1 pedigree of Salix suchowensis; the phenotypic values above wood properties were tested by Anderson-Darling distribution function, and the phenotypic data of the above traits that didn't meet the normal distribution were transformed with BOX-COX function formulae; all phenotypic data could be transformed into normal distribution, therefore, these traits are appropriated for quantitative trait loci analysis. In addition, the correlation analysis among the above traits show that the the hemicellulose content was negatively correlated with cellulose and lignin contents, whereas the basic wood density was positively correlated with the cellulose content, and was negatively correlated with the hemicellulose content.