SiC/MoSi2-SiC-Si Oxidation Protective Coatings for HTR Graphite Spheres with Residual Si Optimized
Xiaoyu Wei,Hui Yang,Hongsheng Zhao,Xiaoxue Liu,Kaihong Zhang,Ziqiang Li,Yuan Gao,Bing Liu
DOI: https://doi.org/10.3390/ma15093203
IF: 3.4
2022-01-01
Materials
Abstract:SiC/MoSi2-SiC-Si coatings for nuclear graphite spheres with different Si-Mo ratios were prepared through two-step pack cementation. XRD, SEM and EDS techniques were used to analyze the composition and microstructure of the coatings. The oxidation resistance performance of the composites at 1773 K, in static air, was investigated. The results showed that the SiC-MoSi2-Si coating could be divided into a denser inner layer and a loose outer layer, as free Si would infiltrate into the inner micropores of the coating under capillary force. When the Si/Mo ratio of the second pack cementation was 7:1, the thickness of the denser inner layer basically reached the maximum and exhibited excellent oxidation resistance ability, with a weight gain of 0.19% after 200 h oxidation. The performance improvement was analyzed as a result of the addition of SiC and C powder in the pack cementation process, effectively increasing the phase interfaces to relax the thermal stress in the coating. With different Si-Mo ratios, the content of residual Si and the formation rate of SiO2 glass layer on the coating surface were also different, thus affecting the anti-oxidation performance. The main reactions occurring at different stages of the oxidation curve were also discussed.