Study on the Preparation and Characterization of the Levofloxacin Hydrochloride and Chitosan Membrane

彭湘红,陈春华

DOI: https://doi.org/10.3969/j.issn.1000-2375.2004.02.014

2004-01-01

Abstract:Used levofolxacin hydrochloride (LF) as model drug, chitosan (CS) as delivery, the membrane with different drug contents and the coated membrane which used chitosan as painting lays were prepared. The interaction between LF and CS and the morphology of membrane were investigated by FTIR, X-ray and SEM. The release behavior of LF and the mechanical properties of the membrane were determined. The results showed that the hydrogen bonding between LF and CS was formed in the membrane. LF was absorbed on the surface of the membrane, and little LF could be seen on the surface of coated membrane. While the contents of LF from 0.5?%(wt) to 2.0?%(wt), the tensile strength and the elastic modulus of membrane were decreased from 29?MPa to 11?MPa and from 2?050?MPa to 626?MPa, respectively. The thickness of coated membrane from 0.15?mm to 0.25?mm, the tensile strength and the elastic modulus of membrane were 26～18?MPa,1?257～75?MPa. About 98?%(wt) of LF was released from coated membrane within 6～13?h in the phosphate buffer solution (pH 5.8).