Abstract:The ductility of metallic materials is recognized to be significantly affected by stress state and strain rate. However, systematic investigations on the impacts of stress state and strain rate on ductile behavior are infrequent, and only a minority of fracture models can consider both effects concurrently. This work aims to systematically investigate the ductile response of Ti6Al4V alloy over a broad spectrum of stress states and strain rates and to propose a ductile model that incorporates the coupled influence of stress state and strain rate. First, five types of specimens were employed to obtain distinct stress states. Then, the fracture strain of material was ascertained for strain rate spanning from 10 −3 /s to 10 3 /s, stress triaxiality ranging from -0.7 to 0.4, and Lode angle parameter varying from -1 to 1 using a combined experimental-numerical method. It was found that over a broad spectrum of stress states, the relation between fracture strain versus stress state is not monotonic, and the fracture strain reduces as strain rate increases. Utilizing the experimental data, a novel ductile fracture model incorporating the stress triaxiality, Lode angle parameter and strain rate was established and embedded into the ABAQUS/Explicit through the user material subroutine VUMAT. Finally, a validation test was conducted to demonstrate the validity of the proposed model. The results indicate the satisfactory correlation between experiment and calculation for fracture displacement and fracture morphology, which illustrates that the proposed model can predict the ductile behavior across a wide spectrum of stress states and strain rates. This work provides a definite theoretical guidance for the optimization design and safety evaluation of Ti-6Al-4V alloy structural components.

The Relation between Failure Models of Steels Used in Pressure Vessel and Stress-State and its Engineering Application

Improved Ultra-Low Cycle Fatigue Fracture Models for Structural Steels Considering the Dependence of Cyclic Damage Degradation Parameters on Stress Triaxiality

Microstructures-based Constitutive Analysis for Mechanical Properties of Gradient-Nanostructured 304 Stainless Steels

A Proposal on Ultra-Low Cycle Fatigue Damage Evaluation of Structural Steels

Ductile Fracture Modelling of Steel Plates under Tensile and Shear Dominated States

A Simple Calibrated Ductile Fracture Model and Its Application in Failure Analysis of Steel Connections

Failure Modeling for QP980 Steel by a Shear Ductile Fracture Criterion

Research on Fatigue-Creep Interaction Damage of Steel 1.25Cr0.5mo

Investigating Ductile Failure At The Microscale In Engineering Steels: A Micromechanical Finite Element Model

A Modified Coffin-Manson Model for Ultra-Low Cycle Fatigue Fracture of Structural Steels Considering the Effect of Stress Triaxiality

Study on micromechanical fracture models of structural steel and its welds

A Ductile Fracture Criterion Based on Three-Dimensional Void Model

Understanding Microstructure-Evolution-dependent Fracture Behaviors in Pearlitic Steels

Modelling of ductile fracture in ship structures subjected to quasi-static impact loads

A Modified Ductile Fracture Model Incorporating Synergistic Effects Of Pressure And Lode Angle

Investigation of the Fracture Behavior of High-Strength Structural Steel and Welds Based on Micromechanical Models

Fracture prediction in transverse fillet welded joints of high strength structural steel

Overview on the Prediction Models for Sheet Metal Forming Failure: Necking and Ductile Fracture

Coupled effect of stress state and strain rate on ductile fracture of Ti6Al4V alloy

Fracture Behavior Evaluation Model for Steel Structural Components Based on Crack Extension Resistance Curves

Approach of failure assessment of pressure vessels containing tilted cracks