Abstract:The study investigated the microstructure and mechanical properties of composite strengthened high-chromium cast iron by laser quenching and laser shock peening. Observation of microstructure, measurement of microhardness, residual stress and FWHM (full width at half maximum), impact toughness and wear tests were carried out on untreated, laser quenched, laser quench-laser shock peened high-chromium cast iron specimens. The research results showed that the laser shock peening will not produce new phases in high-chromium cast iron, and can further promote the transformation of retained austenite into martensite. The grains inside the laser quench-laser shock peened sample were obviously refined, and the carbides were uniformly dispersed. The laser quench-laser shock peened specimen produced large residual compressive stress and FWHM value on the surface, reaching -432.49 MPa and 2.124°, respectively. The problem of residual stress difference between the hardened zone and the transition zone caused by laser quenching was eliminated, and the tensile stress was all converted into compressive stress, which further increases the dislocation density and improves the micro-hardness. The impact toughness value of laser quench-laser shock peened specimen was 4.43 J/cm 2 , which was 16.27% higher than that of the untreated sample. The friction coefficient and wear rate were significantly reduced, and the wear scar was shallow and narrow, showing weak abrasive wear and oxidative wear, the impact toughness and wear resistance of high-chromium cast iron were improved. The results obtained from this study could be used as reference in future research and applications of laser strengthened high-chromium cast iron.

Study on Microstructure and Properties of Laser Melting Unit of HT200

Application Status and Research Progress of Brake Disc Materials for High-speed Train

Mechanical Properties and Fracture Behavior of Laser Powder-Bed-Fused GH3536 Superalloy

Effect Of Laser Melting Processing On The Microstructure And Wear-Resistance Of Gray Cast-Iron

Investigation on Microstructures and Tribological Characteristic of Laser Remelting Layers

Improving the Properties of Gray Cast Iron by Laser Surface Modification

Study on the effects of laser quenching power and scanning speed on the property of cast iron

Laser Melting and Surface Texture Technology: Effect on Friction Properties

Numerical Simulation and Experimental Study on Compound Casting of Layered Aluminum Matrix Composite Brake Drum

Microstructure and mechanical properties of composite strengthened high-chromium cast iron by laser quenching and laser shock peening

Performance of a cast-iron and WC Co-free iron-based coated disc under mild and severe brake conditions

Microstructural Properties of Particle-Reinforced Multilayer Systems of 316L and 430L Alloys on Gray Cast Iron

Microstructure and Properties of Ni-based VC and TiVC2 Composite Coatings Fabricated in Situ by Laser Direct Deposition

Properties of Laser-Clad Stainless Steel–Ni/WC Double-Layer Coatings

Thermal Cracking and Friction Performance of Two Kinds of Compacted Graphite Iron Brake Discs under Intensive Braking Conditions

Investigation on Microstructure and Performance of Boron Cast IronCylinder Liner with Laser Remelting

Evaluation of Thermal Fatigue Life and Crack Morphology in Brake Discs of Low-Alloy Steel for High-Speed Trains

LASER CLADDING ON HIGH AND LOW CONTENT OF CARBON CAST IRON FOR BRAKE DISCS

Microstructure and wear behavior of arc-shaped 40CrNiMo steel after laser hardening

Microstructure Design of Controlling Crack of Fe-based Laser Cladding Layer

Effect of Laser Quenching-Shock Peening Strengthening on the Microstructure and Mechanical Properties of Cr12MoV Steel