Abstract:Two compositions Ce0.50Zr0.39La0.04Y0.07O2−δ and Ce0.25Zr0.65La0.04Y0.06O2−δ based on ceria-zirconia solid solutions were prepared as nanopowders using a continuous hydrothermal flow synthesis reactor, followed by either freeze-drying or hotplate-drying of the slurry. Each dried nanopowder was then subjected to 10h heat-treatment at 1000°C, 1100°C or 1200°C in air (to simulate accelerated ageing). The reducibility and hydrogen consumption of the oxidised samples were measured using temperature programmed reduction (TPR) up to 1000°C. The effects of composition, drying method and heat-treatment temperature were evaluated on the TPR profiles of the materials. The powders were further investigated using a range of analytical methods including UV/Vis spectroscopy (which yielded colour data), Raman spectroscopy, powder X-ray diffraction, BET surface area measurements and X-ray photoelectron spectroscopy (XPS). Chemometric methods were used to investigate relationships between the spectroscopic and total oxygen storage capacity (OSC) data. Principal component analysis (PCA) was used to provide a simple interpretation of the effects of various synthesis and treatment parameters on Raman spectra. Principal component regression (PCR) was used to build regression models relating the Raman spectra and the temperature of hydrogen consumption peak at several set temperatures in the TPR. The total hydrogen consumption of the materials was generally high, while the drying and heat-treatment conditions appeared to have a significant effect on the final properties of the resulting powders, such as the surface area and total oxygen storage capacity.

Study on the Electrical Properties and Mechanism of Nano Yttria-Doped Ceria

Thermal Conductivity and Expansion Coefficient of (Sm0.5Gd0.3Yb0.2)2Ce2O7

Study on Sm2O3 and Nd2O3 Co-doped Ceria Based Electrolyte

Microstructural evolution and its influence on oxygen diffusion in yttrium-doped ceria thin films

Preparation and Properties of Ce0.8Y0.2O1.9 Electrolyte

Synthesis and Characterization of Doped Nano-Sized Ceria–zirconia Solid Solutions

Microstructural and Electrical Changes in Ca0.9R0.1CeNbMoO8 (R = Y, Sm, Nd, La) Ceramics Induced by Rare‐earth Ion Doping

Influence of Yb 2 O 3 on electrical and microstructural characteristics of CaCu 3 Ti 4 O 12 ceramics

Research of Structural, Strength and Thermal Properties of ZrO2—CeO2 Ceramics Doped with Yttrium

Influence of Y2O3 Doping on Phase Evolution and Dielectric Characteristics of ZrO2 Ceramics

Effect of Yttrium Doping on Oxygen Storage Capacity of Ce_(0.33)Zr_(0.67)O_2

Microstructural and electrical changes in Ca 0.9 R 0.1 CeNbMoO 8 ( R = Y, Sm, Nd, La) ceramics induced by rare‐earth ion doping

Effect Of Different Ce2o3 On The Structure And Properties Of Bzt-Ct Ceramics

Nano-dispersed yttria-stabilized zirconia powder: Phase, morphology, and conductivity investigation with different chelating agents via a modified sol-gel method

Electrical Properties of Ceria Co-doped with Sm3+ and Nd3+

Citric–Nitrate Combustion Synthesis and Electrical Conductivity of the Sm3+ and Nd3+ Co‐Doped Ceria Electrolyte

Effect of the Composition of the Ceramics (MCeMgSr)O2-δ (M = Y, Sm) on the Microstructure, Mechanical and Electrical Properties for Solid Electrolyte

Cathodoluminescence and Raman spectroscopic analyses of Nd- or Yb-doped Y2O3 transparent ceramics

Electrical conductivity of mixed conductors (YO1.5) x.(CeO2)y.(ZrO2)1-x-y

Enhanced electrical properties in low-temperature sintering PNN – PMW –PZT ceramics by Yb2O3 doping

Synthesis and Characterization of (gd, Y)-Doped Ceria Electrolytes for Solid Oxide Fuel Cell