Effects of Heat Input on the Microstructure and Property of the High Current MAG Welding Seam

包晔峰,薛小怀,周昀,楼松年,吴毅雄

DOI: https://doi.org/10.3969/j.issn.1000-3738.2004.04.006

2004-01-01

Abstract:Side bend test was carried out at room temperature on the high current MAG welding joints under 15kJ/cm and 28kJ/cm heat input respectively.The experimental results showed that the joints with 28kJ/cm heat input bended with 180° were acceptable,but those with 15kJ/cm failed at a bending angle less than 15°.OM,SEM,EDAX and chemical composition analyses showed that small heat input led to shorter weld pool time,the oxiddation reaction could not complete fully,which resulted in overmuch C,Si and Ti in weldmetal,and brittle and massive bainitic microstructure was formed.All these reduced the joint toughness.In addition,small heat input led to welding pool cooled more quickly,which made the multi-kind oxides escape from the solidifying weldmetal difficultly and inclusions formed.Inclusions reduced the actual sectional area and stress concentration tended to occur there,resulting in crack initiation during the side bend test,which led to brittle fracture finally.With increasing heat input,the C,Si and Ti were lowered and the microstructure was fined in the weldmetal,inclusions also reduced,so that the joint toughness was improved.