Abstract:MoN and MoN-Cu coatings were deposited on the substrates of 304 stainless steel using direct current (DC) magnetron sputtering. The chemical composition and microstructure of the as-prepared MoN and MoN-Cu coatings were analyzed by scanning electron microscopy (SEM), energy dispersive spectrometer (EDS), X-ray diffraction (XRD), transmission electron microscopy (TEM) and X-ray photoelectron spectroscopy (XPS). The hardness and elastic modulus of the coatings were tested by nanoindentation. The tribological performances of both kinds of coatings sliding against Si3N4 ball under dry and PAO oil-lubricated conditions were evaluated using a ball-on-disc wear tester. The characterization results show that both MoN and MoN-Cu coatings exhibit polycrystalline face-centered cubic (FCC) structures. The MoN coating presents an equiaxed crystal growth manner, while the MoN-Cu coating grows in an obvious columnar crystal. The doping of Cu element exhibits the grain refining effect, endowing the MoN-Cu coating with grain size of 9 nm smaller than that of 12 nm for MoN coating. The hardness and elastic modulus of the MoN-Cu were slightly lower than those of the MoN, due to the doping of Cu element into the coating. The tribo-test results show that the MoN-Cu coating presents superior tribological performances than MoN coating under dry and oil-lubricated conditions, which is closely related to a large number of mixed oxides with good lubrication effect generated on the wear surface for the MoN-Cu coating. The produced oxides on the wear interfaces can also prevent the MoN-Cu coating and the counterpart ball from direct contact, which greatly reduces the friction and wear of the composite coating. Finally, the possible wear mechanisms of both kinds of coatings under oil-lubricated conditions were illustrated by schematic model.

Preparation and Friction Properties of Self-lubricating Layer on Bearing Balls by Ball Milling

Synthesis and Characterization of a Self-Lubricating Film on Bearing Balls

The Thermal Stability and Lubricity of Zinc Thiomolybdenate at Temperatures Up to 500°C

Investigation of failure mechanism and modification for film-lubricated precise angular-contact ball bearing

Research on Wear Mechanism of Solid Lubrication Bearing in Vacuum Environment

Self-luricated modification for silicon nitride ceramic ball surface

Surface Engineering Design of Al2O3/Mo Self-Lubricating Structural Ceramics - Part II: Continuous Lubrication Effects of a Three-Dimensional Lubricating Layer at Temperatures from 25 to 800 °C

Effect of ball–material ratio on Cu-Bi mixed powder and self-lubricating material properties

Preparation and tribological properties of Mo/MoS2-Pb-PbS composite films

Mechanical effect of Mo powder in ball milling process

Surface Engineering Design of Alumina/Molybdenum Fibrous Monolithic Ceramic to Achieve Excellent Lubrication in a High Vacuum Environment

Effect of Substrate Material on Tribological Behavior of Sodium Silicate Bonded MoS2 Solid Lubricating Coatings

Effect of Milling Time on Friction Performance of Nano-SiO_2/Cu Composite Materials

Tribological properties of MoS2 coating for ultra-long wear-life and low coefficient of friction combined with additive g-C3N4 in air

In situ formation of spherical MoS 2 particles on high-entropy alloy coating for low friction

MICROSTRUCTURES AND WEAR-RESISTANCE BEHAV-IORS OF FERROUS SULFIDE COATINGS

Microstructure and Tribological Behaviors of MoN-Cu Nanocomposite Coatings Sliding Against Si3N4 Ball under Dry and Oil-Lubricated Conditions

Microstructure Characteristics and Tribological Properties of Gradient Cu-MoS2 Self-Lubricating Coating Fabricated by Selective Laser Melting of Ink-Printed Metal Nanoparticles

Study of the changes in the microstructures and properties of grease using ball milling to simulate a bearing shear zone on grease

Preparation and properties of FeS/iron-based self-lubricating materials by chemical nickel plating-mechanical alloying

Interlayer Texturing for Improving the Tribological Property in Vacuum of Highly Crystallized Molybdenum Disulfide Film