Adhesion and proliferation of marrow mesenchymal stem cells cultured on silk fibroin biomaterial modified with RGD peptide
L Ma,H Wang,SH Yang,ZW Shao,CQ Meng,DY Duan,YJ Li
DOI: https://doi.org/10.3321/j.issn:1673-8225.2007.48.011
2007-01-01
Abstract:Aim: In order to promote the adhesion and proliferation of seed cell in the scaffold materials of ligament tissue engineering, the bioactive GRGDS sequence was synthesized and covalent on the silk film, and the proliferation and adhesion of marrow mesenchymal stem cell (MSC) on the modified scaffold materials with RGD peptide were investigated. Methods: From July 2006 to July 2007, the experiment was carried out in the Central Laboratory and Orthopedic Laboratory, Union Hospital of Tongji Medical College, Huazhong University of Science and Technology. The silk film was prepared on white silkworm, and RGD pepti8e was modified on the surface of silk materials, serving as silk-RGD peptide group. While the silk film without modification and culture plate were taken as silk group and positive control group, respectively. The third generation of MSC was seeded onto the RGD modified silk film, the silk film and the culture plate, and then incubated for 4 hours and 12 hours. In each experiment, the number of adhesive cells was counted by using precipitation method to evaluate the efficiency of cell adhesion; At days 1, 2, 3 and 4 of inoculation, the cell density was calculated and used as index of cell proliferation. MSC was seeded onto the RGD modified silk film and the silk film for 24 hours, the immunofluorescence technique was adopted to label the cell skeleton, and the skeletal tissues were observed with the Laser Confocal Microscopy. Results: After 4 hours and 12 hours culture, the efficiency of cell adhesion in the modified silk scaffold was significantly higher than that on unmodified silk scaffold (P < 0.01), but no significant difference was found between the modified silk scaffold and the culture plate (P > 0.05). There were no significant differences in cellular proliferation among each group for culture of 1 day, 2 days, 3 days and 4 days (P > 0.05). After 24-hour culture, the cells on the modified silk film spread widely, their cytoskeleton was more robust, and intracellular stress fiber appeared evidently. The fluorescence intensity of actin on the modified silk film was significantly higher than that on the unmodified silk film (P < 0.05). Conclusion: RGD peptide modification can enhance the adhesion and spread of MSC to silk scaffold, but no obvious effects are observed in cell proliferation.