Impact of Binder on Strength of Carbon-containing Pellet of High-iron Tailings

LIU Zhen-zhen,SUN Ti-chang,YU Wen,GAO En-xia,XU Cheng-yan,LIU Zhi-guo

DOI: https://doi.org/10.3969/j.issn.0253-6099.2013.06.022

2013-01-01

Abstract:The impact of single and mixed binder of CMC,molasses,starch,bentonite,sodium silicate and standard cement on the strength of pressed pellets of high-iron tailings was studied. Results show that CMC or bentonite used as the binder resulted in green pellets with more than 4 times of dropping,wet compressive strength greater than 40 N,dry compressive strength greater than 180 N; while molasses used as the binder can remarkably increase the strength of dry pellets with more than 20 times of dropping and compressive strength up to 730 N. A high-temperature strength test showed that the compressive strength of pellets dropped sharply at the beginning of roasting,but gradually increased with the occurrence of sintering and metallic iron generation. Results of pellet porosity determination tests showed that pellet porosity also increased quickly at the beginning of roasting,maximally over 50% after being roasted for 5 min. It was finally determined that the mixture of CMC( the mass fraction of 0. 4%) and bentonite( the mass fraction of 8%) is used as an optimal binder combination. After being pressed under such condition,pellet was subjected to the process of direct reduction-magnetic separation,leading to the direct reduced iron( DRI) with a TFe grade of 95. 4% and recovery of 88. 42%.