Investigation of two-body dynamic wear behavior of dental CAD/CAM zirconia ceramic
Zhen-xing GUO,Shao-feng ZHANG,Ya-li SUN,Zhen-zhen ZHANG,Xue-song WANG,Xiao-lei TAN,Yue WANG
DOI: https://doi.org/10.15956/j.cnki.chin.j.conserv.dent.2018.01.005
2018-01-01
Abstract:AIM:To study the time-dependent wear characteristics of CAD/CAM zirconia ceramic in sim-ulated oral environment. METHODS:9 zirconia ceramic cylinders(10 mm in length,3 mm in diameter) as maxillary grinding head were made for 1.28 million cycle wear by uniform circular motion, with mandibular zirconia ceramic specimen as the mached pair. The wear test was performed in artificial saliva, at room temperature using the friction and wear testing machine at 50 N load and rotating speed of 100 r/min and turning radius of 2.5 mm. 10 checkpoints were designed in the wear process,the wear loss and roughness of the specimen surfaces were measured using a non-contact 3D profilometer at each checkpoints and a wear curve was plotted. The worn area was morphologically observed using a SEM at corresponding wear stages. RESULTS:Through whole wear process,the wear curve of zirconia ceram-ic was not linear growth,but showed a trend of 3 characteristic stages:running-in wear stage(0~320,000 cycles), steady wear stage(320,000~800,000 cycles) and severe wear stage(800,000~1,280,000 cycles). The volumn loss was more apparent in the running-in stage and severe wear stage,while developed into the stable wear stage the increasing of wear loss was slow. In running-in stage, the wear surface was with tiny and intensive wear marks, in stable wear stage the wear surface was flat,in severe wear stage a large number of cracks could be found on the wear surface. CONLIUSION:Wear behavior of dental zirconia ceramic under the simulated oral environment can divided into running-in,stable and severe wear stages.