Effect of Anodic Oxidation Condition on the Formation Process and Structure of Alumina Nanoporous Film

王为,朱静,贾法龙,巩运兰

DOI: https://doi.org/10.3969/j.issn.1001-3849.2004.06.003

2004-01-01

Abstract:High purity aluminium was anodized in 3%～5% oxalic acid solution and Pt was used as cathode. Anodization process was carried out under different voltage from 30 Vto 70 V and different reaction temperature from 17℃ to 25℃. Electrochemical computer test stytem was used to collect data and ESEM was used to observe the morphology of nano-pore. Thickness of the alumina film was measured by OLYMPAS PM-10A metalloscope. The effect of anodizing voltage, electrolyte and reaction tempereature on the structure of alumina film was studied.The results show that the growth rate, nano-pore diameter and thickness of alumina film are obviously affected by anodic oxidation condition. Growth rate and nano-pore diameter of the alumina film is increased with the increase in concentration and temperature of the electrolyte solution.