An approach to studying the hot tearing mechanism of alloying elements in ternary Mg-Zn-Al alloys
Bingcheng Li,Jing Zhang,Fawang Ye,Ruyue Tang,Quan Dong,Jianhao Chen
DOI: https://doi.org/10.1016/j.jmatprotec.2023.117980
IF: 6.3
2023-08-01
Journal of Materials Processing Technology
Abstract:An approach to studying the mechanism of each alloying elements in ternary alloys is proposed based on theoretical and experimental verification of Mg-(5−7)Zn-(2−3)Al alloys. The hot tearing susceptibility (HTS) measurement is carried out based on a “T” shape constraint rod casting mold with a temperature and load acquisition system. It shows that the Mg-6/7Zn-3Al alloys have similar HTS to that of AZ91 alloy and the liquid fraction (f l ) of 0.3–0.5 is the critical f l range for hot tearing crack initiating in Mg-Zn-Al alloys. The theoretical calculation of the shrinkage stress/strain concentration and liquid phase properties during solidification effectively explain the mechanism of alloying elements Zn and Al on the HTS. It shows that the shrinkage stress/strain concentration from the critical f l range to the end of solidification decrease with increasing the Zn and Al content, which alleviates the cracks formation or propagation. Meanwhile, alloys with higher Zn and Al content maintain a higher f l before the last stage of solidification, which can improve liquid feeding. However, excessive f l in the last stage of solidification is found to be detrimental to the HTS. Therefore, increasing Al content can further alleviate the HTS by controlling f l in the last stage of solidification. The idea of studying the shrinkage stress/strain concentration and liquid phase properties during solidification could hopefully help clarify the role of alloying elements in HTS and establish a reasonable relation between alloying elements and HTS for multi-element alloys, which contributes to designing hot-crack resistant alloy.
materials science, multidisciplinary,engineering, manufacturing, industrial