Sn Doped TiO2 Nanotube with Oxygen Vacancy for Highly Efficient Visible Light Photocatalysis

Jinliang Li,Xingtao Xu,Xinjuan Liu,Caiyan Yu,Dong Yan,Zhuo Sun,Likun Pan
DOI: https://doi.org/10.1016/j.jallcom.2016.04.080
IF: 6.2
2016-01-01
Journal of Alloys and Compounds
Abstract:Sn doped TiO2 nanotube with oxygen vacancy (V-o-Sn-TiO2) was successfully synthesized via a facile hydrothermal process and subsequent annealing in nitrogen atmosphere. The morphology, structure and photocatalytic performance of V-o-Sn-TiO2 in the degradation of nitrobenzene were characterized by scanning electron microscopy, transmission electron microscopy, X-ray diffraction, Raman spectroscopy, X-ray photoelectron spectroscopy, UV-vis absorption spectroscopy, nitrogen adsorption-desorption and electrochemical impedance spectra, respectively. The inner diameter, outer diameter and specific surface area of V-o-SneTiO(2) are about 5 nm, 15 nm and 235.54 m(2) g(-1), respectively. The experimental results show that the V-o-SneTiO(2) exhibits excellent photocatalytic performance with a maximum degradation rate of 92% in 300 min for nitrobenzene and 94% in 100 min for Rhodamine B and corresponding mineralization rates of 68% and 70% under visible light irradiation. The improved photocatalytic performance is ascribed to the enhanced light absorption and specific surface area as well as the reduced electron-hole pair recombination with the presence of oxygen vacancy and Sn doping in the TiO2 nanotube. (c) 2016 Elsevier B.V. All rights reserved.
What problem does this paper attempt to address?