LB-S&T-16 CONSTRUCTING THE 3D MULTI-SCALE MODIFIED BULBAR URETHRAL SCAFFOLD IN VITRO: A PRELIMINARY STUDY

Chao Feng,Xiang-Guo Lv,Yue-Min Xu,Qiang Fu,Lei Chen,Zhe Li,Hua-Ping Wang

DOI: https://doi.org/10.1016/j.juro.2016.03.097

2016-01-01

Abstract:You have accessJournal of UrologyLate-Breaking S&T Poster1 Apr 2016LB-S&T-16 CONSTRUCTING THE 3D MULTI-SCALE MODIFIED BULBAR URETHRAL SCAFFOLD IN VITRO: A PRELIMINARY STUDY Chao Feng, Xiang-Guo Lv, Yue-Min Xu, Qiang Fu, Lei Chen, Zhe Li, and Hua-Ping Wang Chao FengChao Feng More articles by this author , Xiang-Guo LvXiang-Guo Lv More articles by this author , Yue-Min XuYue-Min Xu More articles by this author , Qiang FuQiang Fu More articles by this author , Lei ChenLei Chen More articles by this author , Zhe LiZhe Li More articles by this author , and Hua-Ping WangHua-Ping Wang More articles by this author View All Author Informationhttps://doi.org/10.1016/j.juro.2016.03.097AboutPDF ToolsAdd to favoritesDownload CitationsTrack CitationsPermissionsReprints ShareFacebookTwitterLinked InEmail INTRODUCTION AND OBJECTIVES Although various novel tissue engineered urethral scaffolds have been reported in the last decade, less reports are focused on the multi-scale structure of scaffold. Therefore, the structure of those scaffolds are quite different from the actual urethral tissue. In this study, we investigate the feasibility of constructing the 3D multi-scale modified bulbar urethral scaffold, which can be similar to the native urethral structure. METHODS Five volunteers’ images about their bulbar urethra were obtained through the ultrasound. Those data were used to reform the 3D digital model of bulbar urethra. By using the indirect 3D printing technique, the mould of individual bulbar urethra was constructed. The silk fibroin solution was cast into this mould and freeze-dry procedure was performed, subsequently. After forming the macro porous scaffold, the Acetobacter xylinum was incubated into the scaffold to assemble the cellulose layer. The mechanical tests were perform in all scaffolds. The details of final scaffold were evaluated by the micro CT and scanning electron microscope. Meanwhile, the details of native bulbar urethral structure was compared with those in the constructed scaffold. RESULTS All scaffold exhibited the ideal mechanical properties. The gross view of the constructed scaffolds was similar to the actual bulbar urethra. In the micro-scale, a typical bilayer structure could be noticed in the scaffold. The pore size of scaffold inner surface was 12.3±2.4μm, which is close to the native urethra (15.2±3.6μm). The pore size of scaffold sublayer and native urethra were 140±34μm and 146±30μm, respectively. In the nano-scale, no statistical difference of fiber diameter was found in the constructed scaffold and native urethra (22.3±6.3 nm vs 24.6±5.0 nm). CONCLUSIONS Our study demonstrated the feasibility of constructing individual 3D urethral scaffold, which was similar to the structure of native bulbar urethra in multi-scale. Furthermore, the structure of this scaffold could be easily modified by controlling the production process according to the demanding of design. It provide a novel conception for constructing the tissue engineering urethral scaffold. © 2016FiguresReferencesRelatedDetails Volume 195Issue 4SApril 2016Page: e342 Advertisement Copyright & Permissions© 2016MetricsAuthor Information Chao Feng More articles by this author Xiang-Guo Lv More articles by this author Yue-Min Xu More articles by this author Qiang Fu More articles by this author Lei Chen More articles by this author Zhe Li More articles by this author Hua-Ping Wang More articles by this author Expand All Advertisement Advertisement PDF downloadLoading ...