Hydrothermal Synthesis of Open-Framework Borophosphates with Tunable Micropore Sizes, Crystal Morphologies, and Thermal Stabilities

Wei Sun,Ya-Xi Huang,Sergiy Nokhrin,Yuanming Pan,Jin-Xiao Mi

DOI: https://doi.org/10.1021/cg5017438

IF: 4.01

2015-01-01

Crystal Growth & Design

Abstract:Thermal stabilities of zeolitic frameworks are important parameters for many applications. Two decades of research have produced only a very small number of zeolitic borophosphates such as Na-2[VO(B2O)(PO4)(2)(HBO3)]center dot xH(2)O (x approximate to 2.92) (denoted as B3P2), Which shows the onset dehydration and a complete decomposition at 200 and 400 degrees C, respectively, In order to enhance thermal stabilities of borophosphate frameworks, a water-deficient hydrothermal route with phosphoric acid as the sole solvent has been developed and led to controlled syntheses of B3P2, and a new vanadium borophosphate, K1.33Na0.67[VO(B2O)center dot(PO4)(2)(HPO4)]center dot xH(2)O (x approximate to 1.63) (denoted as B2P3). The latter is the first-ever borophosphate possessing the zeolite,RHO-type net and is characterized by superlarge spherical cages, including 16-ring and 8-ring channels along the axe and 12-ring channels along the diagonals of the cubic cell. The new compound B2P3 has larger structural cages and higher thermal stability than B3P2, where the enhanced thermal stability is attributable to different bonding arising from the substitution of [BO2(OH)] by [PO3(OH)] in the framework. This is the first demonstration that the micropore size, crystal morphology, and thermal stability of zeolitic borophosphates can be tuned by changing the fundamental building units of their frameworks via adjusting the B/P ratios in the starting materials.