Abstract:<p>For wear resistant steels, there is generally a linear relationship between the initial hardness and wear resistance, yet a high initial hardness limits the formability of components. The intrinsic ductility of austenite and strain hardening produced from the transformation-induced plasticity (TRIP) effect during service opens a new window for this contradiction. Herein, the wear resistance and the corresponding failure mechanisms of 5Mn steels after different heat treatment processes were evaluated using a ball-on-disk sliding test under dry conditions. The wear behaviors of the counterbodies were also studied to elucidate the wear mechanism of the tribo-system. The results show that the microstructures of the hot-rolled and air-cooled steel mainly comprised martensite. When the intercritical annealing temperature was relatively low (<695°C), the microstructure primarily consisted of reversed austenite and ferrite. The samples annealed at 630°C, 645°C, 660°C, and 675°C had a similar initial hardness, while the sample annealed at 675°C possessed a wear resistance that was 3.25 times that of the steel annealed at 630°C. The large difference in the wear resistance was predominately due to the gradient of strain hardening provided by the varied amount and mechanical stability of the retained austenite. The transformation from austenite to martensite, which has an increased hardness, improves the work hardening. A strengthening layer formed with a certain thickness that provided stress support during the wear process and enhanced the wear resistance. When the annealing temperature reached 695°C, a large amount of secondary martensite was generated from austenite that had a low thermal stability, which improved the initial hardness and wear resistance. The steels with a large amount of martensite had an enhanced wear resistance, but the elongation severely deteriorated, leading to unsatisfactory formability. The present work provides guidance for designing novel steels with an excellent balance of good formability and decent wear resistance by precisely adjusting the characteristics of the retained austenite.</p>

Local Plastic Indentation Resistance of Retained Austenite in Bearing Steel

A Study of Deformation Behavior and Stability of Retained Austenite in Carbide-Free Bainitic Steel During Nanoindentation Process

Nanoindentation Investigation on the Mechanical Stability of Individual Austenite Grains in a Medium-Mn Transformation-Induced Plasticity Steel

Deformation Behavior of Retained Austenite and Its Effect on Plasticity Based on In-Situ EBSD Analysis for Transformable Ferritic Stainless Steel

Effect of Different Microstructures on Surface Residual Stress of Induction-Hardened Bearing Steel

Nano-indentation Investigation on the Mechanical Stability of Individual Austenite in High-Carbon Steel

In-Situ Neutron Diffraction and Crystal Plasticity Finite Element Modeling to study the Kinematic Stability of Retained Austenite in Bearing Steels

Investigating the Difference in Mechanical Stability of Retained Austenite in Bainitic and Martensitic High-Carbon Bearing Steels using in situ Neutron Diffraction and Crystal Plasticity Modeling

Inconsistent effects of mechanical stability of retained austenite on ductility and toughness of transformation-induced plasticity steels

Analysis of the Relationship Between Retained Austenite Locations and the Deformation Behavior of Quenching and Partitioning Treated Steels

Indentation of Commercial Pure Titanium Processed by Cold Rolling

Characterization of Retained Austenite in Advanced High-Strength Steel.

Novel Insights into the Contribution of Pretreatment on Mechanical Properties of High Nitrogen Martensitic Bearing Steels

Effect of retained austenite on plasticity and toughness of micro/nano bainitic steel

Nanoindentation Characterization on Local Plastic Response of Ti-6Al-4V under High-Load Spherical Indentation

Quasi-Situ Characterization of Retained Austenite Orientation in Quenching and Partitioning Steel via Uniaxial Tensile Tests

The Role of Retained Austenite on the Mechanical Properties of a Low Carbon 3Mn-1.5Ni Steel

C and Mn Elements Characterization and Stability of Retained Austenite in Different Locations of Quenching and Partitioning Bainite Steels

Effects of Sub-zero Celsius Treatment and Tempering on the Stability of Retained Austenite in Bearing Steel

Unraveling the significant role of retained austenite on the dry sliding wear behavior of medium manganese steel

Probing the Effect of Intragranular Premature Κ-Carbide on Incipient Plasticity Behavior in Austenite-Based Fe-Mn-Al-(Cr)-C Steels