Abstract:Single-phase 2Gd2O3·(Gd,Tb)2(SO4)3·nH2O precursor with strong crystallinity was synthesized by the water-bath method through optimizing the introducing method of Tb3+ doping, where Tb3+ was introduced from Tb(NO3)3. The formation process and phase evolution of the precursor were analyzed in detail. Compared with the conventional method of introducing Tb3+ via Tb4O7, the inhomogeneous doping caused by the appearance of 2Tb2O3·(Gd,Tb)2(SO4)3·nH2O in the precursor was avoided. Pure Gd2O2S:Tb nanopowders with layered structure were obtained after calcination in flowing H2-Ar. The Gd2O2S:Tb powder prepared with Tb(NO3)3 has higher XEL intensity than that with Tb4O7. Using the synthesized powders as starting material, Gd2O2S:Tb scintillation ceramics with high relative density (over 99% of the theoretical value) were fabricated by vacuum pre-sintering and HIP post-treatment in an argon atmosphere. The influences of the introducing method of Tb3+ doping on the microstructure, photoluminescence and X-ray excited luminescence of the Gd2O2S:Tb ceramics were studied. The ceramic sample prepared with Tb(NO3)3 has better luminescence properties due to the homogeneous doping in the ceramics. Temperature-dependent XEL measurements imply that the green emission of the ceramic sample is always dominant with the increase of temperature from 77 K to 340 K, attributed to the cross-relaxation between 5D3 and 5D4 levels of Tb3+.

Sintering and Characterisation of Gd3al3ga2o12/Y3al5o12 Layered Composite Scintillation Ceramic

Design, Simulation, Elaboration and Luminescence of Tb3+-doped Ba0.84Gd0.16F2.16 Fluoroaluminosilicate Scintillating Glass Ceramics

Structural and Scintillation Properties of Ce3+:Gd3Al3Ga2O12 Translucent Ceramics Prepared by One-Step Sintering

Sintering of GGAG:Ce3+, Xy(3+) Transparent Ceramics in Oxygen Atmosphere

Preparation of Ce-Doped Gd3(Al, Ga)5O12 Nanopowders via Microwave-Assisted Homogenization Precipitation for Transparent Ceramic Scintillators

Al2O3–Ce:YAG and Al2O3–Ce:(Y,Gd)AG composite ceramics for high brightness lighting: Effect of microstructure

Microstructure evolution in two-step-sintering process toward transparent Ce:(Y,Gd)3(Ga,Al)5O12 scintillation ceramics

Cation-substitution Induced Stable GGAG:Ce3+ Ceramics with Improved Optical and Scintillation Properties

Ce3+ doped Lu3Al5O12 ceramics prepared by spark plasma sintering technology using micrometre powders: Microstructure, luminescence, and scintillation properties

Preparation of Ce-doped (y,gd)3al5o12 Nanoceramics by Sintering and Crystallization of Glass Microspheres

Effects of Ga Substitution for Al on the Fabrication and Optical Properties of Transparent Ce:Gagg-Based Ceramics

Customizing the luminescent properties of compositionally disordered ceramics (Gd, Y, Yb, Tb, Ce)3Al2Ga3O12: From an ultra-fast scintillator to bright, wide-spectrum phosphor

Preparation and Luminescence Properties of Ce3+/Dy3+-codoped Fluorosilicate Glass Ceramics

Scintillation and Luminescent Properties of the (Gd,Y)3Al2Ga3O12:Ce Ceramics Obtained by Compaction of Green Bodies Using Digital Light Processing 3D Printing

Study of Composite Al2O3-Ce:Y3Mg18Al14Si18O12 Ceramic Phosphors

Scintillation Properties of GAGG:Ce Ceramic and Single Crystal

Fabrication and Characterization of Ce3+-Doped Lithium Alumino-Silicate Scintillating Glass-Ceramic and Fiber

Mechanical, photoluminescent properties and energy transfer mechanism of highly transparent (Y0.99−xGdxSm0.01)2O3 ceramics for scintillator applications

Ce3+, Pr3+ Co-Doped Lu3Al5O12 Single Crystals and Ceramics: A Comparative Study

Fabrication of Gd2O2S:Tb scintillation ceramics from the uniformly doped nanopowder

Preparation and Optical Properties of Mgal2o4/Ce : Yag Transparent Ceramics