Well-dispersed monolayer CrO x /Silicalite-1 catalysts for efficient propane dehydrogenation
Lili Cai,Yongzheng Zhao,Xiaoyan Tian,Dandan Qin,Cunzi Wei,Xue Cai,Wenling Chu,Weishen Yang
DOI: https://doi.org/10.1016/j.cej.2024.152925
IF: 15.1
2024-06-13
Chemical Engineering Journal
Abstract:To reduce the loading of environmentally unfriendly Cr, well-dispersed monolayer CrO x catalysts supported on silicalite-1 (S-1) were successfully prepared for propane dehydrogenation (PDH), and the effect of the K promoter was also systematically investigated. The characterization results demonstrated that Cr 6+ species were dominant at Cr loadings less than 3 wt%, which seemed to be responsible for the better PDH performance at a rather low Cr content through reducing Cr 6+ to active Cr 3+ species during the PDH process. At Cr loadings ≥5 wt%, the Cr species tended to form aggregates such as crystalline α-Cr 2 O 3 , which has been found to be unfavourable for PDH activity. The enhanced PDH performance of the 2Cr-0.5 K catalyst (2 wt% Cr 2 O 3 , 0.5 wt% K 2 O) prepared by coimpregnating Cr and K was mainly attributed to the elimination of the medium and strong acid sites of the catalysts for inhibiting coke formation. Moreover, the 2Cr-0.5 K catalyst exhibited a complete recovery of PDH activity after regeneration, which was attributed to the easy removal of coke at lower temperatures. More importantly, the well-dispersed monolayer catalyst (2Cr/S-1) achieves propane conversion up to 51.2 % and a space–time yield of propene formation up to 0.35 kg C3H6 h −1 kg cat. −1 at 580 °C and has the lowest Cr content among previously reported Cr-based catalysts with comparable performance. This study might provide insight for achieving low Cr loading and high PDH activity to minimize the effect of toxic Cr and maximize process economics.
engineering, chemical, environmental