Excellent Cryogenic Optical Thermometry Based On Green Up-Conversion Of Ho3+-Doped Perovskite Na0.5bi0.5tio3 Ceramics
Yuzhen Wang,Yanan Wang,Chaoyang Ma,Zhe Feng,Chuandong Zuo,Wanggui Ye,Chong Zhao,Yanbin Li,Zicheng Wen,Zhiquan Cao,Zhijun Cao,Xiaofei Shen,Chong Wang,Yingkui Li,Xuanyi Yuan,Yongge Cao
DOI: https://doi.org/10.1039/d0tc04906a
IF: 6.4
2021-01-01
Journal of Materials Chemistry C
Abstract:In this study, various Na0.5Bi0.5TiO3:0.5 at% Ho3+ (NBT:Ho) ceramics with different Yb3+ ion doping concentrations were synthesized by a conventional solid-state reaction method. Under the irradiation of a 980 nm laser, the NBT:Ho sample exhibited four distinguished emission bands centered at 525, 548, 656, and 753 nm. By co-doping Yb3+ ions into NBT as the sensitizers, the up-conversion luminescence of Ho3+ ions was greatly enhanced. The mechanism for up-conversion luminescence was determined to be a two-photon absorption process. The DFT simulations revealed that the Ho3+ 4f orbitals pass through the Fermi level and thus f-f transitions could be highly sensitive to temperature variation. Green emissions at 525 and 548 nm were ascribed to the two thermally coupled excited states F-5(4) and S-5(2) transferring to the ground state I-5(8), respectively. The temperature-dependent population between F-5(4) and S-5(2) could be interpreted by Boltzmann's distribution in the range of 167-377 K. The relative sensitivities were calculated to be 6.14% K-1 at 167 K and 1.03% K-1 at 377 K, and the corresponding absolute sensitivities were estimated to be 0.09 x 10(-3) K-1 and 2.11 x 10(-3) K-1, respectively. The temperature resolution was calculated to be about 0.053 K at 167 K and 0.319 K at 377 K. The excellent repeatability of the NBT:Ho3+ ceramics was demonstrated by means of successive heating-cooling cycles in the range of 167-377 K. The above investigation results demonstrate the promising application of NBT:Ho in cryogenic optical thermometers.