Ordered Mesoporous Nickel Sphere Arrays for Highly Efficient Electrocatalytic Water Oxidation

Tingting Sun,Lianbin Xu,Yushan Yan,Anvar A. Zakhidov,Ray H. Baughman,Jianfeng Chen

DOI: https://doi.org/10.1021/acscatal.5b02571

IF: 12.9

2016-01-01

ACS Catalysis

Abstract:We report the preparation and use of the three-dimensionally ordered mesoporous Ni sphere arrays (3D-OMNiSA) as a highly effective OER catalyst in alkaline electrolyte. The 3D-OMNiSA is fabricated through lyotropic liquid crystal templating within a polymer inverse opal. The prepared 3D-OMNiSA catalyst exhibits a low overpotential of 254 mV at 10 mA cm(-2) and a small Tafel slope of 39 mV decade(-1), better than the commercial precious RuO2 catalyst. The mass activity (166.5 A g(-1)) and turnover frequency (0.0281 s(-1)) of 3D-OMNiSA are about 4.3 and 2.2 times that of RuO2, respectively. Additionally, this 3D-OMNiSA catalyst shows a high durability under harsh water oxidation cycling test. The outstanding OER performance of the 3D-OMNiSA could be attributed to the large surface area, efficient mass and charge transport, and high structural stability arising from the unique 3D hierarchical porous structure of the 3D-OMNiSA consisting of ordered close-packed mesoporous spheres.