One Key Issue in Characterization of Organic Solar Cells with Solution Processed Interfacial Layers

Jinhua Gao,Qiaoshi An,Miao Zhang,Jianli Miao,Xiaoling Ma,Zhenghao Hu,Jianxiao Wang,Fujun Zhang

DOI: https://doi.org/10.1039/c9cp00181f

2019-01-01

Abstract:Solution processed interfacial layers are commonly employed in bulk heterojunction organic solar cells (OSCs) for better charge collection. PDIN interfacial layers were prepared by employing a static or dynamic spin coating method from PDIN methanol solution, and defined as the S-PDIN or D-PDIN layer. The OSCs with a S-PDIN layer exhibit 13.88% power conversion efficiency (PCE) with a virtual high short circuit density (J(SC)) of 26.45 mA cm(-2) and relatively low fill factor (FF) of 58.94% during the current density versus voltage (J-V) measurement without a shadow mask. 12.56% PCE is achieved for OSCs with a D-PDIN layer, along with a J(SC) of 18.85 mA cm(-2) and FF of 74.88%. Over 77% FFs are obtained for OSCs with a S-PDIN or D-PDIN layer during J-V measurement with a shadow mask, and both OSCs exhibit a very similar J(SC) and PCE. The virtual high J(SC)s and relatively low FF of OSCs with a S-PDIN layer may be due to the enhanced conductivity of PEDOT:PSS during preparation of the PDIN layer by the SSC method, which can be further confirmed from the OSCs with a methanol treated PEDOT:PSS layer. This work indicates that a well-balanced J(SC) and FF should be an important evaluating indicator for efficient OSCs, and an appropriate shadow mask is necessary to measure the J-V curves of OSCs with a solution processed interfacial layer.