Partition Of Alloying Elements Between Gamma-(A1), Gamma(')-(L12), And Beta-(B2) Phases In Ni-Al Base Systems
c c jia,k ishida,tsutomu nishizawa
DOI: https://doi.org/10.1007/BF02651589
1994-01-01
Abstract:Phase equilibria between gamma (A1), gamma' (L1(2)), and beta (B2) phases in the Ni-rich portions of the Ni-Al-X ternary systems were investigated over a temperature range of 800-degrees-C to 1300-degrees-C. The tie lines and phase boundaries were accurately determined by the diffusion couple technique. It was established that Co, Cu, Mn, Fe, and Cr concentrated more into the gamma phase than into the gamma' phase, while Ta, Nb, Ti, V, and Si mostly partitioned to the gamma' phase. The partition coefficients for alloying elements between gamma and gamma' phases varied as a function of temperature for most of the elements and also as a function of concentration for some of the elements, such as Mo, W, and V. In the equilibrium between gamma' and beta phases, Mn, Fe, Co, and Cu partitioned to the beta phase rather than to the gamma' phase, whereas Nb, Mo, Ta, Ti, W, V, Cu, and Si concentrated into the gamma' phase. The partition of alloying elements in the metastable equilibrium between gamma and beta phases, in the Ni-Al binary system, was estimated from the data on gamma/gamma' and gamma'/beta equilibria. Based on these data, the relative stabilizing effects of alloying elements on gamma, gamma', and beta phases are also discussed.