Abstract:Single-crystal a-iron oxide (denoted as FO) particles with uniform sub-micrometer size and polyhedron-like shape have been successfully fabricated by using polyvinylpyrrolidone (PVP) capping agent-mediated hydrolysis of iron nitrate under mild hydrothermal conditions (200 degrees C). The hematite products were characterized via combined techniques including scanning electronic microscopy (SEM), X-ray diffraction (XRD), and transmission electron microscopy (TEM). The single-crystal hematite particles have relatively uniform sizes of 180-360 nm and octahedron-shaped structures with comparatively smooth surfaces. Furthermore, the as-made hematite particles can be used as cores to prepare core-shell mesoporous silica composites. The intermediate nonporous silica layer was coated first via a sol-gel process, and then the mesoporous silica structure was coated as the outer shell layer by a surfactant-assembly method, resulting in uniform core-shell mesoporous silica FO@nSiO(2)@mSiO(2) composites. TEM images show that the FO@nSiO(2)@mSiO(2) composites possess distinct two-layer coating core-shell structures with ordered hexagonal mesostructure in the outer silica shell layer. N-2 sorption measurements show that the uniform accessible mesochannel size for the FO@nSiO(2)@mSiO(2) nanocomposites is similar to 2.10 nm, the surface area is as high as similar to 445m(2)/g, and the pore volume is as large as similar to 0.29 cm(3)/g. Furthermore, the reflection loss (dB) spectra measured in the frequency range 2-18 GHz showed that the FO@nSiO(2)@mSiO(2) composites have improved electromagnetic interference (EMI) shielding effectiveness (SE) compared to that of pure hematite materials. This is mainly attributed to the better impedance match and multiple-interfacial polarization among the FO@nSiO(2)@mSiO(2) nanocomposites.

Facile Synthesis of Uniform Hollow Hematite Sub-Micro Spheres with Controllable Shell Thickness

Novel And Facile Method For The Preparation Of Monodispersed Titania Hollow Spheres

Synthesis and Magnetic Properties of Uniform Hematite Nanocubes

Hematite Hollow Spindles and Microspheres: Selective Synthesis, Growth Mechanisms, and Application in Lithium Ion Battery and Water Treatment

Magnetite Fe3O4 Nanoparticles and Hematite Α-Fe2o3 Uniform Oblique Hexagonal Microdisks, Drum-Like Particles and Spindles and Their Magnetic Properties

A Simple Approach to the Synthesis of Hollow Microspheres with Magnetite/Silica Hybrid Walls

Hydrothermal synthesis and characterization of core/shell ALOOH microspheres

Hematite Hollow Spheres with a Mesoporous Shell: Controlled Synthesis and Applications in Gas Sensor and Lithium Ion Batteries

Synthesis of Hematite Particles with Various Shapes by A Simple Hydrothermal Reaction

Synthesis and Magnetic Properties of Biocompatible Hybrid Hollow Spheres.

Highly Shape-Selective Synthesis, Silica Coating, Self-Assembly, And Magnetic Hydrogen Sensing Of Hematite Nanoparticles

Monodisperse Magnetic Core/shell Microspheres with Pd Nanoparticles-Incorporated-carbon Shells.

Synthesis and Microwave Absorption of Uniform Hematite Nanoparticles and Their Core-Shell Mesoporous Silica Nanocomposites

A Facile Colloidal Templating Method to Monodisperse Hollow Ag and Ag/Au Submicrometer Spheres

Sandwich Fe2o3@Sio2@Ppy Ellipsoidal Spheres and Four Types of Hollow Capsules by Hematite Olivary Particles

Hematite Nanostructures Synthesized by A Silk Fibroin-Assisted Hydrothermal Method

Monodisperse Ba0.6Sr0.4TiO3 hollow spheres via a modified template-assisted method

Facile precipitation microfluidic synthesis of Monodisperse and inorganic hollow microspheres for Photocatalysis

Hollow Iron Oxide Nanospheres Obtained through a Combination of Atomic Layer Deposition and Electrospraying Technologies

Facile Fabrication Method And Characterization Of Hollow Ag/Sio2 Double-Shelled Spheres

Use of Carbonaceous Polysaccharide Microspheres As Templates for Fabricating Metal Oxide Hollow Spheres