Enhanced Photoelectric Property of Mo-C Codoped TiO 2 Films Deposited by RF Magnetron Cosputtering

Shengyun Luo,Bingxi Yan,Jie Shen
DOI: https://doi.org/10.1007/s11595-017-1584-z
2017-01-01
Abstract:Mo-C codoped TiO 2 films were prepared by RF magnetron cosputtering. Ultraviolet-visible spectroscopy, atomic force microscopy, X-ray photoelectron spectroscopy, energy dispersive X-ray Analysis and X-Ray Diffraction were used to study the influences of codoping on energy gap, surface morphology, valence states of elements, ions content and crystal structure, respectively. The concentration of photogenerated carriers was measured by studying photocurrent density, while catalytic property was evaluated by observing degradation rate of methylene blue under visible light. A Mo-doped TiO 2 film, whose content of Mo had been optimized in advance, was prepared and later used for subsequent comparisons with codoped samples. The result indicates that Mo-C codoping could curtail the energy gap and shift the absorption edge toward visible range. Under the illumination of visible light, codoped TiO 2 films give rise to stronger photocurrent due to smaller band gaps. It is also found that Mo, C codoping results in a porous surface, whose area declines gradually with increasing carbon content. Carbon and Molybdenum doses were delicately optimized. Under the illumination of visible light, sample doped with 9.78at% carbon and 0.36at% Mo presents the strongest photocurrent which is about 8 times larger than undoped TiO 2 films, and about 6 times larger than samples doped with Mo only.
What problem does this paper attempt to address?