Abstract:The present study reports a simple, template free and controllable one-step synthesis of a series of amorphous, crystalline, and triphasic TiO 2 nanoparticles utilizing titanium( IV ) ethoxide as a molecular precursor. By reacting the titanium ethoxide in a mixture of ethanol, acetic acid, and water at reflux temperatures while varying the ratios of the reaction components, it was possible to obtain TiO 2 nanoparticles possessing high surface areas and pore volumes as well as diverse crystalline structures. The synthesized nanoparticles were characterized by FT-IR, XRD, SEM, TEM, TG, DTA, DTG, DRS, and argon sorption. X-ray diffraction and sorption analyses conclusively show that using an excess of ethanol resulted in the formation of an amorphous TiO 2 with a high surface area. Furthermore, an increase in the water content while slightly reducing the amount of acid but keeping ethanol still at excess resulted in the formation of a crystalline anatase phase, whereas the reaction in the absence of ethanol led to the formation of a triphasic material consisting of anatase (40.5%), rutile (25.5%), and brookite (34%). Under the optimized conditions, it was possible to produce amorphous and crystalline porous titanium dioxide with high surface areas of 350 and 310 m 2 g −1 respectively at low temperatures without subsequent heat treatment, which is reflected in their catalytic properties. Investigation of the photocatalytic and catalytic abilities of the synthesized nanoparticles to degrade and to reduce methylene blue (MB), respectively, as well as reduction of nitroaromatic compounds in aqueous media revealed that the amorphous materials showed the best performance with degradation of up to 94–99% of MB within 10 minutes. The kinetic studies also revealed that all nanoparticles exhibited high catalytic activity for the reduction of MB within a short time (3–4 min) and showed good agreement with a pseudo-first-order reaction model. The derived rate constants for the catalytic reduction of 2-NP, 3-NP, 4-NP, 2-NA, and 3-NA (NP = nitrophenol and NA = nitroaniline) with amorphous TiO 2 nanoparticles ( Ti-9 ), as the best catalyst, are 0.67 min −1 , 0.24 min −1 , 1.46 min −1 , 0.56 min −1 , and 0.21 min −1 , respectively. From the data, we can deduce that a high specific surface area, the occurrence of defects as well as the crystallinity of the materials play an essential role in the photocatalytic and catalytic performance.

Aerosol Spray Pyrolysis Synthesis of Porous Anatase TiO 2 Microspheres with Tailored Photocatalytic Activity

Soft-chemical Synthesis of Mesoporous Nitrogen-Modified Titania with Superior Photocatalytic Performance under Visible Light Irradiation

Spray pyrolysis synthesis and UV-driven photocatalytic activity of mesoporous Al2O3@TiO2 microspheres

Template-free Hydrothermal Synthesis of Macroporous TiO2 Microspheres on a Large Scale

Self-assembly and Photocatalysis of Mesoporous TiO 2 Nanocrystal Clusters

A Novel Etching and Reconstruction Route to Ultrathin Porous TiO2 Hollow Spheres for Enhanced Photocatalytic Hydrogen Evolution

Interface Actions Between TiO2 and Porous Diatomite on the Structure and Photocatalytic Activity of TiO2-diatomite

Preparation of SiO2@Au@TiO2 Core–shell Nanostructures and Their Photocatalytic Activities under Visible Light Irradiation

Alkaline hydrothermal synthesis of homogeneous titania microspheres with urchin-like nanoarchitectures for dye effluent treatments.

Simple preparation of sub-micron mesoporous TiO2 spheres consisting of anatase nanocrystals

Synthesis of TiO2 Hollow Spheres with Tunable Pore Structure and Enhanced Photocatalytic Activity

Hierarchical Nanosheet-Assembled Yolk–shell TiO2microspheres with Improved Photocatalytic Activity

Mesoporous hollow sphere titanium dioxide photocatalysts through hydrothermal silica etching

Synthesis and Characterization of Anatase TiO2 Microspheres Self-Assembled by Ultrathin Nanosheets

Anatase-TiO2 nano-particle preparation with a micro-mixing technique and its photocatalytic performance

Scalable Synthesis of Mesoporous Titania Microspheres Via Spray-Drying Method.

Synthesis of Uniform Ordered Mesoporous TiO2 Microspheres with Controllable Phase Junctions for Efficient Solar Water Splitting

One-Step Synthesis of Hierarchically Porous Hybrid Tio2 Hollow Spheres with High Photocatalytic Activity

Controllable and facile one-pot synthesis of high surface area amorphous, crystalline, and triphasic TiO2: catalytic and photocatalytic applications

Sonochemical Synthesis and Photocatalytic Activity of Meso- and Macro-Porous TiO(2) for Oxidation of Toluene.

Formation of hollow porous TiO2 nanospheres via the encapsulation of CO2 nanobubbles for high-performance adsorption and photocatalysis