Enhanced Electromechanical Strain Response in (Fe0.5nb0.5)4+-Modified Bi0.5(Na0.8K0.2)0.5TiO3 Lead-Free Piezoelectric Ceramics

Yu-Kai Lv,Shao-Feng Duan,Zhi-Hao Zhao,Xin-Yu Kang,Rui-Fang Ge,Hongqiang Wang,Yejing Dai

DOI: https://doi.org/10.1007/s10853-018-2147-1

IF: 4.5

2018-01-01

Journal of Materials Science

Abstract:By the traditional solid-state reaction method, Bi0.5(Na0.8K0.2)0.5Ti1−x(Fe0.5Nb0.5) x O3 (marked as BNKT-xFN; x = 0.00, 0.01, 0.02, 0.03 and 0.04) piezoelectric ceramics were fabricated, and the effects of FN substitution on the dielectric, ferroelectric, piezoelectric and electric field-induced strain performance were investigated. The relative dielectric permittivity and loss tangent reveal that the phase transition temperature between ferroelectric and ergodic relaxor phase is reduced from 90 °C to room temperature (RT), even below RT, with increasing FN content. Temperature dependence of polarization–electric field loops and strain-electric field curves exhibits that the ferroelectric order is disturbed gradually, and the ergodic relaxor phase forms with increasing FN content. A large unipolar strain of 0.42% and corresponding d33* (= Smax/Emax) of 642 pm/V for the sample with x = 0.04 are obtained under 6.5 kV/mm due to the phase transition from ergodic relaxor to ferroelectric. These results indicate that the (Fe0.5Nb0.5)4+ complex ion-modified BNKT-based ceramics would have great potentials for lead-free electromechanical actuator applications.