Abstract:We report on a red-emitting ScVO4:Bi3+ phosphor which does not show excitation at energies below 2.88 eV (430 nm). X-ray diffraction, time-resolved, and quantitative photoluminescence (PL) spectroscopy were employed to characterize relations between crystal structure and luminescence properties of the material. Results show that incorporation of Bi3+ renders the blue photoemission of blank ScVO4 to red. Dynamic luminescence analysis between 10 and 300 K reveals a complicated dependence of energy transfer from VO43- groups to Bi3+ ions and population redistribution of P-3(1) and P-3(0) of Bi3+ on temperature. This reflects in distinct changes in the luminescence decay functions. That is, a dramatic decrease of Bi3+ luminescence lifetime occurs from hundreds to only several microseconds. Density functional theory is employed to reveal how the unusual red Bi3+ luminescence comes, and results indicate that the perturbation of oxygen vacancies which is generated readily when bismuth precipitates into ScVO4 is the reason for the experimental observation, although the vacancies themselves do not show photoluminescence. Upon excitations at 330 and 380 nm, internal quantum efficiencies can be up to similar to 56% and similar to 47%, respectively, implying the potential application of the red phosphor in warm-white-light-emitting diodes. As a proof of concept, an exemplary device was developed by combining the present phosphor with an ultraviolet-light-emitting diode and a commercial phosphor (Ba, Eu)MgAl10O17:Mn. We obtain a color rendering index (CRI) of >90 and a color temperature of similar to 4306 K at chromaticity (0.3744, 0.3991).

Efficient Red-Emitting Phosphor ScVO4 Doped with Bi3+ and Eu3+ for Near-Ultraviolet-activated Solid-State Lighting

Efficient Red-Emitting Phosphor for Near-Ultraviolet-based Solid-State Lighting

Luminescent Properties of LuVO4:Eu3+,Bi3+ Red Phosphor for Light-Emitting Diodes.

Red Photoluminescence from Bi3+ and the Influence of the Oxygen-Vacancy Perturbation in Scvo4: A Combined Experimental and Theoretical Study

Red-Shift Of Vanadate Band-Gap By Cation Substitution For Application In Phosphor-Converted White Light-Emitting Diodes

A novel red phosphor Ca12Al14O32Cl2:Eu3+ for near UV white light-emitting diodes

Intense red-emitting NaYSiO4: Eu3+, Mo6+ phosphors for white light-emitting diodes

Eu3+ doped (Y0.75Sc0.25)2O3 red-emitting ceramics with excellent photoluminescence properties for LEDs

Enhanced Red Emission From Eu3+-Bi3+ Co-Doped Ca2ysbo6 Phosphors For White Light-Emitting Diode

A new red-emitting phosphor of Eu3+-doped Sr 2MgMoxW1-xO6for solid state lighting

Photoluminescence properties and energy transfer in the Sm3+ and Eu3+ co-doped Ca3Bi(PO4)3 red phosphor

Synthesis and luminescence properties of YVO4:Eu3+,Bi3+ phosphor with enhanced photoluminescence by Bi3+ doping

Structure, luminescence properties and anti-thermal quenching of a novel Eu3+-activated red phosphor based on the negative thermal expansion material In0.5Sc1.5(MoO4)3

Photoluminescence of β-Ba2ScAlO5: Eu3+ red emitting phosphors effectively activated by UV light

Gd3B(W,Mo)O9: Eu3+ Red Phosphor: from Structure Design to Photoluminescence Behavior and Near-Uv White-Leds Performance

Synthesis and luminescent properties of a novel red-emitting phosphor: Eu3+-activated Ba2ScO3F

A red phosphor LaSc3(BO3)4:Eu3+ with zero-thermal-quenching and high quantum efficiency for LEDs

Deep‐Red (Sr,Ba)Lu2O4: Eu2+ Phosphor for Full‐Spectrum Lighting

A novel efficient red-emitting K7SrY2B15O30: Eu3+ phosphor with non-concentration quenching and robust thermal stability for white LEDs

A Potential Red-Emitting Phosphor for LED Solid-State Lighting

An Efficient Charge Compensated Red Phosphor Sr3WO6: K+, Eu3+ – for White LEDs