Enhanced Wettability of Zinc Passivation Layer by Coating Organic–inorganic Multilayers

Xiao-Dan Shao,Li-Qun Zhu,Wei-Ping Li,Hai-Ning Chen,Hui-Cong Liu

DOI: https://doi.org/10.1007/s12598-017-0989-3

IF: 6.318

2023-01-01

Rare Metals

Abstract:Zinc Cr(III) passivation layer (Zn-PL) could effectively protect NdFeB materials from corrosion. However, long-term exposure of Zn-PL to ambient atmosphere would reduce its wettability spontaneously, which hinders or deteriorates the adhesion of post-deposited materials. To solve this issue, a multilayer developed by layer-by-layer assembly approach was designed, and alumina sol and silica sol were prepared. A polyacrylic acid (PAA) layer was firstly deposited on Zn-PL to remove the preabsorbed organic carbon and form poly(zinc acrylate). Then, Al2O3 and SiO2 sol–gel layers were sequentially assembled on PAA-coated Zn-PL. As a result, the hydrophobic Zn-PL turns into super-hydrophilic by coating organic–inorganic multilayers, which is attributed to the surface enrichment of hydrophilic hydroxyl groups and increases surface roughness. Furthermore, the super-hydrophilic surface displays excellent adhesion property without the negative effect on its other properties, which highlights a good prospect for a wide application of NdFeB or other potential materials.