Abstract:Porous structure is an efficient tool for optimizing the elastic modulus and osseointegration properties of titanium alloy materials. However, the investigations on pore shape remain scarce. In this study, we created porous Ti6Al4V scaffolds with a pore size of 600 μm but different lattices (cubic pentagon, diamond, cuboctahedron). The mechanical and biological properties of the scaffolds were investigated in static simulation analysis, in vitro mechanical compression test, computational fluid dynamics, as well as cell and animal experiments. The results demonstrated that the calculated yield strength difference between the three Ti6Al4V porous scaffolds was negligible, at approximately 140 MPa, allowing them to match the strength requirements of human bones. The diamond scaffold has the lowest calculated elastic modulus (11.6 GPa), which is conducive for preventing stress shielding. The shear stress was largely concentrated in the diamond scaffold, and the stress range of 120–140 MPa accounted for the greatest share. The mouse MC3T3-E1 cells were found to attach to all three scaffolds, with the diamond scaffold displaying a higher degree of cell adherence. There was more proliferating cells on the diamond and cubic pentagon scaffolds than on the cuboctahedron scaffolds (P < 0.05). The diamond scaffold exhibited the highest alkaline phosphatase activity and calcium salt accumulation in cell differentiation tests. Besides, the expression of osteogenic genes on the diamond scaffold was higher than that on the cuboctahedron scaffold, the cubic pentagon scaffold displaying the lowest expression. The in vivo studies revealed that all three scaffolds fused well with the surrounding bone and that there was no loosening or movement of the prosthesis. Micro-computed tomography, corroborated by the staining results of hard tissues, revealed that the level of new bone formation was the highest in the diamond scaffold, followed by the cuboctahedron scaffold (P < 0.05). Taken together, the diamond scaffold is comparatively better at optimizing the elastic modulus and osseointegration properties of titanium alloy materials, and thus is a preferred choice for porous design.

In vitro and in vivo comparisons of the porous Ti6Al4V alloys fabricated by the selective laser melting technique and a new sintering technique.

Mechanical properties and in vitro cytocompatibility of dense and porous Ti–6Al–4V ELI manufactured by selective laser melting technology for biomedical applications

Preparation, Characterization and Designing of Porous Ti–6Al–4V Through Metal Injection Molding Without Space Holder

Experimental Study of Performance of Ti-6Al-4V Femoral Implants Using Selective Laser Melting (SLM) Methodology

Comparison of 3D-printed porous tantalum and titanium scaffolds on osteointegration and osteogenesis

Trabecular-like Ti-6Al-4V Scaffolds for Orthopedic: Fabrication by Selective Laser Melting and in Vitro Biocompatibility

Preparation and mechanical performance analysis of porous Ti6Al4V scaffold fabricated by direct ink writing

In Vitro and In Vivo Analysis of the Effects of 3D-Printed Porous Titanium Alloy Scaffold Structure on Osteogenic Activity

In Vitro and in Vivo Study of Selective Laser Melted Porous Ti-Ta-Nb-Zr Scaffolds for Repairing Bone Defects

Effect of lattice type on biomechanical and osseointegration properties of 3D-printed porous Ti6Al4V scaffolds

Mechanical and Electrochemical Corrosion Behaviors of Porous Ti-6Al-4V Alloys Prepared by an Electrochemical Sintering Approach

Ti6Al4V biomimetic scaffolds for bone tissue engineering:Fabrication, biomechanics and osseointegration

Study of Bone Regeneration and Osteointegration Effect of a Novel Selective Laser-Melted Titanium-Tantalum-Niobium-Zirconium Alloy Scaffold

Ti6Al4V biomimetic scaffolds for bone tissue engineering: Fabrication, biomechanics and osseointegration

Laser beam melting 3D printing of Ti6Al4V based porous structured dental implants: fabrication, biocompatibility analysis and photoelastic study

Fabrication and characterization of selective laser melting printed Ti–6Al–4V alloys subjected to heat treatment for customized implants design

Microstructure and biocompatibility of porous-Ta/Ti-6Al-4 V component produced by laser powder bed fusion for orthopedic implants

In Vitro and in Vivo Study of Additive Manufactured Porous Ti6Al4V Scaffolds for Repairing Bone Defects

Influence of porosity on osteogenesis, bone growth and osteointegration in trabecular tantalum scaffolds fabricated by additive manufacturing

Mechanical property of Ti6Al4V cylindrical porous structure for dental implants fabricated by selective laser melting

In vitro evaluation of the biocompatibility and bioactivity of a SLM-fabricated NiTi alloy with superior tensile property