Abstract:Graphdiyne (GDY) is an artificial carbon allotrope that is conceptually similar to graphene but composed of sp‐ and sp2‐hybridized carbon atoms. Monolayer GDY (ML‐GDY) is predicted to be an ideal two‐dimensional (2D) semiconductor material with a wide range of applications. However, its synthesis has posed a significant challenge, leading to difficulties in experimentally validating theoretical properties. Here, we report that in‐situ acetylenic homocoupling of hexaethynylbenzene within the sub‐nanometer interlayer space of MXene can effectively prevent out‐of‐plane growth or vertical stacking of the material, resulting in ML‐GDY with in‐plane periodicity. The subsequent exfoliation process successfully yields free‐standing GDY monolayers with micrometer‐scale lateral dimensions. The fabrication of field‐effect transistor on free‐standing ML‐GDY makes the first measurement of its electronic properties possible. The measured electrical conductivity (5.1×103 S m−1) and carrier mobility (231.4 cm2 V−1 s−1) at room temperature are remarkably higher than those of the previously reported multilayer GDY materials. The space‐confined synthesis using layered crystals as templates provides a new strategy for preparing 2D materials with precisely controlled layer numbers and long‐range structural order. This article is protected by copyright. All rights reserved

High‐Yield and Damage‐free Exfoliation of Layered Graphdiyne in Aqueous Phase

Ultrathin Graphdiyne Film on Graphene Through Solution-Phase Van Der Waals Epitaxy

Catalyst‐Free Synthesis of Few‐Layer Graphdiyne Using a Microwave‐Induced Temperature Gradient at a Solid/Liquid Interface

Novel Cyclic Ultrasound-Assisted Liquid Phase Exfoliation of Graphene in Deionized Water: A Parameter Study

Exploring Approaches for the Synthesis of Few‐Layered Graphdiyne

Scalable synthesis of soluble crystalline ionic-graphdiyne by controlled ion expansion

Rapid synthesis of few-layer graphdiyne using radio frequency heating and its application for dendrite-free zinc anodes

Crystalline monolayer graphdiyne synthesized in the MXene interlayer space

Effect of Static Pressure on Ultrasonic Liquid Phase Exfoliation of Few-Layer Graphene

Advancement In Liquid Exfoliation Of Graphite Through Simultaneously Oxidizing And Ultrasonicating

Controlled Growing of Graphdiyne Film for Friction Reduction and Antiwear

New Synthetic Methods towards Graphdiyne

Recent progress and challenges in crystalline graphdiyne

Glue-assisted grinding exfoliation of large-size 2D materials for insulating thermal conduction and large-current-density hydrogen evolution

Exfoliated Graphdiyne for the Electroless Deposition of Au Nanoparticles with High Catalytic Activity.

Mechanical Exfoliation of Two-Dimensional Materials

Interlayer catalytic exfoliation realizing scalable production of large-size pristine few-layer graphene

Defect-Free Single-Layer Graphene by 10 S Microwave Solid Exfoliation and Its Application for Catalytic Water Splitting

High-Yield Production of Few-Layer Graphene via New-fashioned Strategy Combining Resonance Ball Milling and Hydrothermal Exfoliation

Space‐Confined Synthesis of Monolayer Graphdiyne in MXene Interlayer

Aqueous cellulose solution assisted direct exfoliation of graphite to high concentration graphene dispersion