Twin-Directed Deposition of Pt on Pd Icosahedral Nanocrystals for Catalysts with Enhanced Activity and Durability toward Oxygen Reduction
Mingkai Liu,Zhiheng Lyu,Yu Zhang,Ruhui Chen,Minghao Xie,Younan Xia
DOI: https://doi.org/10.1021/acs.nanolett.1c00007
IF: 10.8
2021-02-18
Nano Letters
Abstract:Platinum nanocrystals featuring a multiply twinned structure and uniform sizes below 5 nm are superb catalytic materials, but it is difficult to synthesize such particles owing to the high twin-boundary energy (166 mJ/m<sup>2</sup>) of Pt. Here, we report a simple route to the synthesis of such nanocrystals by selectively growing them from the vertices of Pd icosahedral seeds. The success of this synthesis critically depends on the introduction of Br<sup>–</sup> ions to slow the reduction kinetics of the Pt(II) precursor while limiting the surface diffusion of Pt adatoms by conducting the synthesis at 30 °C. Owing to the small size and multiply twinned structure of Pt dots, the as-obtained Pd–Pt nanocrystals show remarkably enhanced activity and durability toward oxygen reduction, with a mass activity of 1.23 A mg<sup>–1</sup><sub>Pt</sub> and a specific activity of 0.99 mA cm<sup>–2</sup><sub>Pt</sub>, which are 8.2 and 4.5 times as high as those of the commercial Pt/C.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acs.nanolett.1c00007?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acs.nanolett.1c00007</a>.Synthetic protocols; TEM image of the Pd icosahedral seeds; size distribution of Pt dots; time-elapsed TEM images of Pd–Pt great icosahedra; TEM images of Pd–Pt nanocrystals synthesized with different amounts of K<sub>2</sub>PtCl<sub>4</sub>, without Br<sup>–</sup>, or at a higher temperature; and CV and ORR polarization curves recorded from the commercial Pt/C catalyst before and after different cycles of ADT (<a class="ext-link" href="/doi/suppl/10.1021/acs.nanolett.1c00007/suppl_file/nl1c00007_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.
materials science, multidisciplinary,chemistry, physical,physics, applied, condensed matter,nanoscience & nanotechnology