Development of composite magnesium oxychloride cement and its application on solidification of dredged sludge
Boxiang Huang,Junxin Liu,Wei Tang,Junrun Li,Bin Li,Anhui Wei
DOI: https://doi.org/10.1016/j.conbuildmat.2024.135587
IF: 7.4
2024-03-04
Construction and Building Materials
Abstract:The dredging sludge from river channels is a challenging task due to its low strength and high compressibility, and the use of magnesium oxychloride cement (MOC) for curing treatment has a high sustainability value. In this regard, the synergistic solidification efficiency of magnesium oxychloride cement (MOC), along with the selected additives (e.g., sodium silicate, CFBC desulfurization ash, and silica fume), on tested sludge was systematically evaluated by the Unconfined Compressive Strength (UCS) and microstructural tests. Initially, the baseline component ratio of MOC solidified sludge was determined through analyzing the effect of the water content, MOC cement dosage and molar ratio of MgO/MgCl 2 on its solidification strength. Subsequently, a suitable dosage range for each additive was obtained by observing the UCS's growth behavior for MOC solidified sludge containing a single additive. Then, the regression model for predicting the UCS was formulated using the Response Surface Methodology (RSM), and by interrogating it, can optimize additive contents in terms of the UCS requirements. To collect the experiential data, twenty mix designs with different sodium silicate contents ( x 1 : [4%, 8%]), silica fume contents ( x 2 : [2%, 6%]) and CFBC desulfurization ash contents ( x 3 : [2%, 6%]) were generated by Central Composite Design (CCD). Finally, the phase composition and microstructure differences of composite MOC solidified sludge, MOC solidified sludge and undisturbed sludge were compared to reveal the solidification mechanism of composite MOC cement on tested sludges. The results shows that a specific component mixing ratio (MOC cement: sodium silicate: silica fume: CFBC desulfurization ash) of composite MOC cement for satisfying maximum solidification strength is 10: 5.35: 5.34: 3.45. The strength performance of composite MOC solidified sludge is superior to that of MOC solidified sludge, as evidenced by the presence of numerous flocculent hydrated products such as phase 5(5[Mg(OH) 2 ]·MgCl 2 ·8(H 2 O)), M-S-H and C-S-H gels in composite MOC solidified sludge, while only short rod-like phase 5 being detected in MOC solidified sludge. Herein, a conceptual model on the sludge solidification using composite MOC cement was also innovatively developed.
construction & building technology,materials science, multidisciplinary,engineering, civil