Engineering Heterostructure-Incorporated Metal Silicates Anchored on Carbon Nanotubes for Highly Durable Lithium Storage
Qiushi Wang,Yuhang Li,Tao Meng,Binbin Huang,Lei Hu,Hongjie Su,Changgong Meng,Yexiang Tong
DOI: https://doi.org/10.1021/acsaem.0c02738
IF: 6.4
2021-01-20
ACS Applied Energy Materials
Abstract:Although transition metal silicates are recognized as high potential and attractive materials for next-generation lithium-ion batteries (LIBs) due to their efficient energy storage, earth-abundance without pollution, low cost, and easy preparation, however, the unstable electrochemical stability originating from the intrinsic mechanism involved in long-term cycling tests is always of concern and needs to be decoupled stepwise. Herein, a strategy is proposed to overcome the challenges through the construction of a heterostructure using a facile hydrothermal method in combination with carbon nanotubes (CNTs), the composite. By tailoring a capacitive contribution over diffusion toward total charge storage in the heterostructure, CNT-coated heterostructural copper–nickel silicates () were employed as the anode to achieve a relatively high capacity (412 mAh g<sup>–1</sup> at 0.2 A g<sup>–1</sup>) and prolonged life for durable LIBs (91% retention after 1000 cycles at 0.5 A g<sup>–1</sup>). The heterostructure generated by NiSi/CuSi could lower the polarization of the composite and elevate its cycle stability, rendering the metal silicate favorable for LIBs. As a consequence, the practical application is evaluated by assembling a full cell based on as the anode and LiNi<sub>0.8</sub>Co<sub>0.1</sub>Mn<sub>0.1</sub>O<sub>2</sub> (NCM811) as the cathode yielding a reversible capacity of 429 mAh g<sup>–1</sup>, along with a decent capacity retention of 221 mAh g<sup>–1</sup> at a current density of 0.5 A g<sup>–1</sup> after 300 cycles. This strategy opens an avenue for constructing long-life metal silicate-based nanocomposites for LIBs.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acsaem.0c02738?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acsaem.0c02738</a>.FESEM images of CNT and <sub>2</sub>, TEM images of <sub>2</sub>, and the corresponding EDS mapping of <sub>2</sub> (Figure S1); FESEM and TEM images of and and the element mapping images (Figure S2); XRD patterns of CNT and <sub>2</sub> (Figure S3); XPS full spectra of , , and (Figure S4); CV curves of , , and (Figure S5); GCD curves of , , and (Figure S6); XRD and TEM results of , , and after cycling (Figure S7); XPS spectra of after 150 cycles (Figure S8); EIS spectra of , , and (Figure S9); electrochemical performance of NCM (Figure S10); EIS for the NCM|| full cell (Figure S11); FESEM, XRD, and element mapping results of and and rate performance of and (Figure S12); summary of EDS analysis (Table S1); structural parameters of all the products obtained by N<sub>2</sub> adsorption–desorption isotherms (Table S2); and comparison of the electrochemical performance (Table S3) (<a class="ext-link" href="/doi/suppl/10.1021/acsaem.0c02738/suppl_file/ae0c02738_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.
materials science, multidisciplinary,chemistry, physical,energy & fuels