Boosting Hydrogen Evolution Reaction Activities of Three-Dimensional Flower-like Tungsten Carbonitride via Anion Regulation
Hong Chuan Fu,Qing Zhang,Juan Luo,Li Shen,Xiao Hui Chen,Li Li Wu,Wan Hui Guo,Yu Xian Yang,Nian Bing Li,Hong Qun Luo
DOI: https://doi.org/10.1021/acssuschemeng.0c04773
2020-08-24
Abstract:Exploring high active, durable, and earth-abundant electrocatalysts for sustainable hydrogen production is a necessary prerequisite of the future hydrogen economy. Herein, anion regulation of a three-dimensional (3D) flower-like tungsten-based heterostructure supported on nickel foam is demonstrated to play a crucial role in boosting the catalytic performance of hydrogen evolution reaction (HER). At high temperature (700 °C), the volatile CN<i><sub>x</sub></i> species decomposed from urea are captured by WO<sub>3</sub> on the nickel foam, and then, the insufficient nitridation and carbonization occurred simultaneously, forming an N-doped W<sub>2</sub>C/WC heterostructure (N-W<sub>2</sub>C/WC-700). The resulting N-W<sub>2</sub>C/WC array exhibits a small overpotential of 63 mV at a current density of 10 mA cm<sup>–2</sup> and a low Tafel slope of 73 mV dec<sup>–1</sup> in alkaline media, accompanied by a negligible loss after 60 h. This work highlights a potentially facile solid-state synthesis strategy for controllable anion regulation and the rational design of the 3D self-supporting carbonitrides, which may provide a feasible interface engineering strategy for constructing other advanced energy materials.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acssuschemeng.0c04773?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acssuschemeng.0c04773</a>.Experimental details; SEM images of the WO<sub>3</sub> precursor; XRD patterns of WO<sub>3</sub>, WO<i><sub>x</sub></i>-400, WON-500, WN-600, N-WO<sub>2</sub>-700, N-W<sub>2</sub>C-700, N-W<sub>2</sub>C/WC-700, W<sub>2</sub>C-700, W<sub>2</sub>C/WC-700, and WC-800; XPS survey and CV curves of WO<sub>3</sub>, WO<i><sub>x</sub></i>-400, WON-500, WN-600, N-W<sub>2</sub>C/WC-700, and N-WC-800 arrays; high-resolution W 4f, N 1s, and C 1s XPS spectra of the N-W<sub>2</sub>C/WC-700 array before and after the cycling test; XRD patterns of the N-W<sub>2</sub>C/WC-700 array after a 60 h stability test; TEM images of the N-W<sub>2</sub>C/WC-700 array after a 60 h stability test; HER polarization curves of N-W<sub>2</sub>C/WC-700, N-W<sub>2</sub>C-700, and N-WC-800 arrays; HER performance of N-W<sub>2</sub>C/WC-700, W<sub>2</sub>C/WC-700, N-W<sub>2</sub>C-700, W<sub>2</sub>C-700, N-WC-800, and WC-800 arrays; and comparison of HER activity data for tungsten nitride/carbide-based catalysts in 1.0 M KOH (<a class="ext-link" href="/doi/suppl/10.1021/acssuschemeng.0c04773/suppl_file/sc0c04773_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.
chemistry, multidisciplinary,engineering, chemical,green & sustainable science & technology