Abstract:Developing high performance electrocatalysts to improve the sluggish kinetics of oxygen reduction reaction (ORR) at the cathode is essential in expanding fuel cell applications. Metal organic frameworks (MOFs), given their high surface area, tunable pore size, and diverse metal choices, are promising candidates to catalyze such a reaction. Herein, we report a family of nine 2D-phthalocyanine MOF-based catalysts for alkaline ORR, where M = Co, Ni, Cu. Structurally, these bimetallic materials have two distinct metal sites, where M1 is a phthalocyanine moiety and M2 is a node, existing as M-N4 moiety. X-ray Diffraction (XRD) shows that all as-prepared MOFs have similar structures and inter-layer spacing. X-ray Photoelectron Spectroscopy (XPS) shows slight shifts in binding energy when the same element is placed in a M1 or M2 site, which indicates that the M1 and M2 sites are chemically distinct. Through cyclic voltammetry we evaluate the role of the metal sites for ORR activity and selectivity in 0.1 M KOH. All materials are active for alkaline ORR, while Ni (M1) – Co (M2) has the best overall kinetic activity performance of - 5 mA cm-2 at 0.7 V vs. RHE. Cu – Cu, on the other hand, is the least active combination under the same testing conditions. Within composition series where M2 = Co, the activity trend for M1 is Ni > Cu ~ Co. From a 2-electron selectivity perspective, M1 = Ni > Cu > Co. From these general trends we hypothesize that Co M2 and Ni M1 sites are essential in promoting 4- and 2-electron selectively, respectively. On average we find a nominal ORR performance trend where M2 = Co > Cu > Ni. Interestingly, we note that the M1 identity also plays a non-linear role in activity and selectivity modulation. Though we identify one of the metal sites (M1 or M2) as the dominating site for activity and/or selectivity, the other site also contributes to the total performance. The density functional theory (DFT) calculation supports our experimental results and finds out that Ni as M1 is highly selective for H2O2 formation whereas Co as M2 shows excellent activity for ORR. Our predicted volcano plot shows that MOF with Ni – Co and Cu – Co combinations at Co active site offering lowest ORR overpotential among all other combinations, which is also in good agreement with experimental findings. By evaluating different metal sites performance through electrochemical testing, we can better understand the active species in the MOF catalytic system. By pairing theory with experiment, we gain active site insight to design new specific enhanced active motifs. We believe that these performance trends can assist in better designing efficient MOF-based ORR catalysts that can lead to advances in clean energy technology for sustainable development.

Nonpyrolyzed Fe-N Coordination-Based Iron Triazolate Framework: an Efficient and Stable Electrocatalyst for Oxygen Reduction Reaction.

Engineering D-Band Center of FeN4 Moieties for Efficient Oxygen Reduction Reaction Electrocatalysts

Directly Converting Fe-doped Metal–organic Frameworks into Highly Active and Stable Fe-N-C Catalysts for Oxygen Reduction in Acid

An ultra-dispersive, nonprecious metal MOF–FeZn catalyst with good oxygen reduction activity and favorable stability in acid

Efficient Fe-Co-N-C Electrocatalyst Towards Oxygen Reduction Derived from a Cationic Co(II)-based Metal-Organic Framework Modified by Anion-Exchange with Potassium Ferricyanide.

Nitrogen-carbon-encapsulated Fe3C nanoparticles as highly efficient earth-abundant oxygen reduction electrocatalysts

Efficient Oxygen Reduction Reaction (ORR) Catalysts Based on Single Iron Atoms Dispersed on a Hierarchically Structured Porous Carbon Framework

Covalent Triazine Framework Anchored with Atomically Dispersed Iron As an Efficient Catalyst for Advanced Oxygen Reduction

Fe, N-decorated Three Dimension Porous Carbonaceous Matrix for Highly Efficient Oxygen Reduction Reaction

FeCo‐oxalate Organic Framework as an Efficient Electrocatalyst for Oxygen Evolution Reaction

Nitrogen-carbon-encapsulated Fe 3 C Nanoparticles As Highly Efficient Earth-Abundant Oxygen Reduction Electrocatalysts

Direct thermal annealing synthesis of FeO nanodots anchored on N-doped carbon nanosheet for long-term electrocatalytic oxygen reduction

Exploring Efficient Fe/N/C Electrocatalysts for Oxygen Reduction from Nonporous Interpenetrated Metal–Organic Framework Involving in Situ Formation of ZnO Templates

Atomically FeN2 Moieties Dispersed on Mesoporous Carbon: A New Atomic Catalyst for Efficient Oxygen Reduction Catalysis

Transition Metal Oxide/ Metal-Organic Framework Hybrid Structures for Efficient Bifunctional Oxygen Electrocatalysis in Alkaline Environments

Fe/N-Doped Carbon Framework Derived from ZIF-8 on Graphene Oxide for Efficient Oxygen Reduction Reaction

High performance Fe–N–C oxygen reduction electrocatalysts by solid-phase preparation of metal–organic frameworks

MOF-Derived Fe-N-C Electrocatalyst via a Dual Ligand Strategy for Efficient Oxygen Reduction in Acidic Media

Carbonized nanoscale metal-organic frameworks as high performance electrocatalyst for oxygen reduction reaction.

Using 2D-Phthalocyanine Metal Organic Framework-Based Catalysts for Oxygen Reduction Reaction in Alkaline Media

Novel Two-Dimensional Metal Organic Frameworks: High-Performance Bifunctional Electrocatalysts for OER/ORR