Abstract:The high cost of precursors and the complexity of synthesis procedures have hindered the widespread use of two-dimensional (2D) porous carbon nanosheets in water splitting. In this study, we successfully developed a low-cost method for the rapid synthesis of three-dimensional (3D) hierarchically porous architectures self-assembled from iron–copper nanoparticles embedded in boron (B)/nitrogen (N)-codoped 2D porous carbon nanosheets (denoted as FeCu@BNPCNS). The optimal FeCu@BNPCNS-900 nanosheet exhibited a large surface area, abundant porous channels, meso/macropores, and carbon edges/defects. Particularly, 10.25 atom% of B/N electrochemically active centers (such as pyridinic-N (including the metal–nitrogen–carbon species), pyrrolic-N, graphitic-N, and BC 3 ) were successfully doped into the optimal FeCu@BNPCNS-900 nanosheets. In an alkaline solution, FeCu@BNPCNS-900 exhibited excellent electrocatalytic activity for hydrogen evolution reaction (HER), which was higher than that of the commercial 20 wt% Pt/C. For example, the HER potential of FeCu@BNPCNS-900 at 10 mA cm −2 [ E 10 ; −202.3 mV vs. reversible hydrogen electrode (RHE)] was only 140.2 mV more negative than that of 20 wt% Pt/C (−62.1 mV vs. RHE). Additionally, FeCu@BNPCNS-900 exhibited a slightly lower oxygen evolution reaction (OER) electrocatalytic activity than the ruthenium oxide (RuO 2 ). Particularly, the OER E 10 potential (+1.634 V vs. RHE) of FeCu@BNPCNS-900 was only 76 mV more positive than that of RuO 2 (+1.558 V vs. RHE). The FeCu@BNPCNS-900||FeCu@BNPCNS-900 cell achieved 10 mA cm −2 at 1.613 V, which was 58 mV more negative than that of the 20 wt% Pt/C||RuO 2 cell (1.671 V). The excellent water-splitting performance of FeCu@BNPCNS-900 could be attributed to the 3D hierarchically porous architecture, abundant channels/mesopores, and uniformly dispersed electrocatalytically active sites. Therefore, we developed an efficient strategy for the large-scale and low-cost synthesis of 2D porous carbon nanosheets without the need for precursors, templates, or surfactants.

Controllable Synthesis of Carbon Nanosheets Derived from Oxidative Polymerisation of M-Phenylenediamine.

A Very Thin Layer of NiO, Ni(OH)2 Nanosheets Arrays with Organic Functional Modification of Polyaniline

Size-Controlled Synthesis Of Pd Nanosheets For Tunable Plasmonic Properties

Oxygen-containing Groups and P Doped Porous Carbon Nitride Nanosheets Towards Enhanced Photocatalytic Activity.

Controllable Synthesis of Polyoxovanadate-Based Coordination Polymer Nanosheets with Extended Exposure of Catalytic Sites

Facile Synthesis of Pd Nanosheets and Implications for Superior Catalytic Activity

Synthesis of Ultrathin PdCu Alloy Nanosheets Used as a Highly Efficient Electrocatalyst for Formic Acid Oxidation.

Two-dimensional Confined Topotactic Transformation to Produce Co-Pi/Co3O4 Hybrid Porous Nanosheets for Promoted Water Oxidation

Solution-based self-assembly synthesis of two-dimensional-ordered mesoporous conducting polymer nanosheets with versatile properties

Molecular Engineering toward High‐Crystallinity Yet High‐Surface‐Area Porous Carbon Nanosheets for Enhanced Electrocatalytic Oxygen Reduction

Controlled Synthesis of N-Doped Carbon Nanospheres with Tailored Mesopores through Self-Assembly of Colloidal Silica.

Facile synthesis of ultrathin metal-organic framework nanosheets for Lewis acid catalysis

Two-Dimensional Polyphosphazene Nanosheet-Derived N,P Doubly Doped Carbon Nanotubes for Electrocatalytic Oxygen Reduction

MOF-Mediated Fabrication of Porous 3-D Superstructure of Carbon Nanosheets Decorated with Ultrafine Cobalt Phosphide Nanoparticles for Efficient Electrocatalysis.

Two-dimensional metal (oxy)hydroxide and oxide ultrathin nanosheets via liquid phase epitaxy

Two-dimensional confined topotactic transformation to produce Co-Pi/Co 3 O 4 hybrid porous nanosheets for promoted water oxidation

Controllable Assembly of Pd Nanosheets: a Solution for 2D Materials Storage

Chemically Robust, Cu-based Porous Coordination Polymer Nanosheets for Efficient Hydrogen Evolution: Experimental and Theoretical Studies

Iminodiacetonitrile induce-synthesis of two-dimensional PdNi/Ni@carbon nanosheets with uniform dispersion and strong interface bonding as an effective bifunctional eletrocatalyst in air-cathode

MOF-Mediated Fabrication of a Porous 3D Superstructure of Carbon Nanosheets Decorated with Ultrafine Cobalt Phosphide Nanoparticles for Efficient Electrocatalysis and Zinc-Air Batteries

High-density defect-induced ultrahigh boron and nitrogen doping of iron–copper-functionalized porous carbon nanosheets for enhanced water splitting