Abstract:Objectives: To design and prepare silk fibroin/hyaluronic acid composite hydrogel. Methods: The thiol modified silk fibroin and the double-bond modified hyaluronic acid were rapidly cured into gels through thiol-ene click polymerization under ultraviolet light condition. The grafting rate of modified silk fibroin and hyaluronic acid was characterized by 1H NMR spectroscopy; the gel point and the internal microstructure of hydrogels were characterized by rheological test and scanning electron microscopy; the mechanical properties were characterized by compression test; the swelling rate and degradation rate were determined by mass method. The hydrogel was co-cultured with the cells, the cytotoxicity was measured by the lactate dehydrogenase method, the cell adhesion was measured by the float count method, and the cell growth and differentiation on the surface of the gel were observed by scanning electron microscope and fluorescence microscope. Results: The functional group substitution degrees of modified silk fibroin and hyaluronic acid were 17.99% and 48.03%, respectively. The prepared silk fibroin/hyaluronic acid composite hydrogel had a gel point of 40-60 s and had a porous structure inside the gel. The compressive strength was as high as 450 kPa and it would not break after ten cycles. The water absorption capacity of the composite hydrogel was 4-10 times of its own weight. Degradation experiments showed that the hydrogel was biodegradable, and the degradation rate reached 28%-42% after 35 d. The cell biology experiments showed that the cytotoxicity of the composite gel was low, the cell adhesion was good, and the growth and differentiation of the cells on the surface of the gel were good. Conclusions: The photocurable silk fibroin/hyaluronic acid composite hydrogel can form a gel quickly, and has excellent mechanical properties, adjustable swelling rate and degradation degree, good biocompatibility, so it has promising application prospects in biomedicine.

Preparation and characterization of aminated hyaluronic acid/oxidized hydroxyethyl cellulose hydrogel.

Preparation and Properties of Carboxymethyl Chitosan/oxidized Hydroxyethyl Cellulose Hydrogel.

Preparation and Characterization of Polysaccharide-Based Hydrogels for Cutaneous Wound Healing

Preparation, Characterization and the Effect of Carboxymethylated Chitosan–cellulose Derivatives Hydrogels on Wound Healing

Injectable, Self-Healing, Antibacterial, and Hemostatic N,O-carboxymethyl Chitosan/oxidized Chondroitin Sulfate Composite Hydrogel for Wound Dressing.

Double-Cross-Linked Hydrogel Strengthened by UV Irradiation from a Hyperbranched PEG-Based Trifunctional Polymer

The preparation and biocompatible evaluation of injectable dual crosslinking hyaluronic acid hydrogels as cytoprotective agents

Antimicrobial and Biocompatible Ε-Polylysine–γ-poly(glutamic Acid)–based Hydrogel System for Wound Healing

Preparation and properties of cellulose nanocrystals, gelatin, hyaluronic acid composite hydrogel as wound dressing

Nonionic polymer cross-linked chitosan hydrogel: preparation and bioevaluation.

Preparation and characterization of PVA/SA/HA composite hydrogels for wound dressing

Preparation, Characterization, and Biocompatibility Evaluation of Poly(nɛ-Acryloyl-l-lysine)/hyaluronic Acid Interpenetrating Network Hydrogels.

Preparation and Characterization of Acid Resistant Double Cross-Linked Hydrogel for Potential Biomedical Applications.

By Endowing Polyglutamic Acid/Polylysine Composite Hydrogel with Super Intrinsic Characteristics to Enhance its Wound Repair Potential

Facile Strategy to Construct a Self-Healing and Biocompatible Cellulose Nanocomposite Hydrogel Via Reversible Acylhydrazone

Synthesis and Characterization of Lignosulfonate- Graft -Poly (acrylic Acid)/hydroxyethyl Cellulose Semi-Interpenetrating Hydrogels

Hyaluronic Acid/Gelatin-Based Multifunctional Bioadhesive Hydrogel Loaded with a Broad-Spectrum Bacteriocin for Enhancing Diabetic Wound Healing

Preparation of silk fibroin/hyaluronic acid composite hydrogel based on thiol-ene click chemistry

Tannic acid/polyvinyl alcohol/2-hydroxypropyl trimethyl ammonium chloride chitosan double-network hydrogel with adhesive, antibacterial and biocompatible properties

Preparation of a chitosan/carboxymethyl chitosan/AgNPs polyelectrolyte composite physical hydrogel with self-healing ability, antibacterial properties, and good biosafety simultaneously, and its application as a wound dressing

In Situ Forming Hydrogel of Natural Polysaccharides Through Schiff Base Reaction for Soft Tissue Adhesive and Hemostasis.